Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_161-2_2_139039_mWDh09.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 26.38 T-atoms per nm^3
Material density = 2.632 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6699 Angstrom
T1  -- O2  = 1.7491 Angstrom
T1  -- O3  = 1.6728 Angstrom
T1  -- O1  = 1.6653 Angstrom
      mean = 1.6893 Angstrom
        t1 = 0.095923  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.073190  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6068 Angstrom
T2  -- O3  = 1.6236 Angstrom
T2  -- O4  = 1.5652 Angstrom
T2  -- O4  = 1.5614 Angstrom
      mean = 1.5893 Angstrom
        t1 = 0.099454  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.074566  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5614 A <--> 1.7491 A
          Mean   = 1.6393 A
          StdDev = 0.0594 A

       t1 Range  = 0.0959 <-- 0.0977 --> 0.0995
       t2 Range  = 0.0732 <-- 0.0739 --> 0.0746

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 104.913 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 125.769 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 102.597 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 108.060 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 126.266 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  =  91.090 deg; O3  -- O1  = 2 A
       91.090 deg <-- 109.783 deg --> 126.266 deg

O2  -- T2  -- O3  = 127.361 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 119.406 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  =  95.629 deg; O2  -- O4  = 2 A
O3  -- T2  -- O4  =  85.586 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 121.613 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 107.585 deg; O4  -- O4  = 3 A
       85.586 deg <-- 109.530 deg --> 127.361 deg

        O-T-O SUMMARY
          Range  = 85.5863 deg <--> 127.3611 deg
          Mean   = 109.6564 deg
          StdDev = 13.9020 deg

        O--O SUMMARY
          Range  = 2.1667 A <--> 3.0461 A
          Mean   = 2.6617 A
          StdDev = 0.2566 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 143.346 deg; T2  -- T2  = 5.6198 A
T2  - O1  - T1  - O3  - T1  = 124.438 deg; T2  -- T1  = 5.3925 A
T2  - O1  - T1  - O1  - T1  = 117.350 deg; T2  -- T1  = 5.2066 A
T2  - O2  - T1  - O3  - T1  =  92.121 deg; T2  -- T1  = 4.3157 A
T2  - O2  - T1  - O1  - T1  =  76.333 deg; T2  -- T1  = 3.7047 A
T1  - O3  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 3.0830 A

T1  - O2  - T2  - O3  - T2  = 113.588 deg; T1  -- T2  = 4.9113 A
T1  - O2  - T2  - O4  - T2  =  79.136 deg; T1  -- T2  = 3.7404 A
T1  - O2  - T2  - O4  - T1  = 160.142 deg; T1  -- T1  = 5.8314 A
T2  - O3  - T2  - O4  - T2  =  60.000 deg; T2  -- T2  = 2.8570 A
T2  - O3  - T2  - O4  - T1  =  79.969 deg; T2  -- T1  = 3.7047 A
T2  - O4  - T2  - O4  - T1  =  96.934 deg; T2  -- T1  = 4.3157 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 160.1418 deg
          Mean   = 100.2797 deg
          StdDev = 30.8280 deg

        T--T SUMMARY
          Range  = 2.8570 A <--> 5.8314 A
          Mean   = 4.3902 A
          StdDev = 0.9626 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 135.153 deg ; T1  -- T1   3.0830 A

T1  -- O2  -- T2  = 127.617 deg ; T1  -- T2   3.0120 A

T1  -- O3  -- T2  = 123.808 deg ; T1  -- T2   2.9080 A

T2  -- O4  -- T2  = 132.060 deg ; T2  -- T2   2.8570 A


        T-O-T SUMMARY
          Range  = 123.8076° <--> 135.1530 deg
          Mean   = 129.6595 deg
          StdDev = 4.4042 deg

        T--T SUMMARY
          Range  = 2.8570 A <--> 3.0830 A
          Mean   = 2.9650 A
          StdDev = 0.0900 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.1667 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 8 16 32 49 70 101 135 166 212 262 305 359 427 489 550
TD10 = 794
Circuit symbol = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31
Vertex symbol  = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 8 16 32 49 70 101 135 166 212 262 305 359 427 489 550
TD10 = 794
Circuit symbol = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31
Vertex symbol  = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31

<TD10> = 794.000
Average ring size = 6.3871