Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_161-2_1_7_RKmMW9.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 2.0545 Angstrom
T1  -- O2  = 1.6369 Angstrom
T1  -- O2  = 1.8968 Angstrom
T1  -- O2  = 1.8968 Angstrom
T1  -- O1  = 1.9231 Angstrom
      mean = 1.8816 Angstrom

        T-O SUMMARY
          Range  = 1.6369 A <--> 2.0545 A
          Mean   = 1.8816 A
          StdDev = 0.1379 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  83.026 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  = 122.775 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  75.998 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  = 119.257 deg; O1  -- O1  = 3 A
O2  -- T1  -- O2  = 134.201 deg; O2  -- O2  = 3 A
O2  -- T1  -- O2  = 134.201 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  =  68.464 deg; O2  -- O1  = 2 A
O2  -- T1  -- O2  =  90.887 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  = 115.226 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  =  87.080 deg; O2  -- O1  = 3 A
       68.464 deg <-- 103.112 deg --> 134.201 deg

        O-T-O SUMMARY
          Range  = 68.4644 deg <--> 134.2014 deg
          Mean   = 103.1116 deg
          StdDev = 23.5911 deg

        O--O SUMMARY
          Range  = 2.0166 A <--> 3.4695 A
          Mean   = 2.8895 A
          StdDev = 0.4796 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 155.418 deg ; T1  -- T1   3.8865 A

T1  -- O2  -- T1  = 116.762 deg ; T1  -- T1   3.0122 A
T1  -- O2  -- T1  = 116.762 deg ; T1  -- T1   3.0122 A
T1  -- O2  -- T1  = 121.093 deg ; T1  -- T1   3.3033 A


        T-O-T SUMMARY
          Range  = 116.7623° <--> 155.4182 deg
          Mean   = 127.5090 deg
          StdDev = 16.5587 deg

        T--T SUMMARY
          Range  = 3.0122 A <--> 3.8865 A
          Mean   = 3.3035 A
          StdDev = 0.3646 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.0166 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.3033 Angstrom
  T1  -- T1  = 3.3033 Angstrom
  T1  -- T1  = 3.0122 Angstrom
  T1  -- T1  = 3.0122 Angstrom
  T1  -- T1  = 3.0122 Angstrom
  T1  -- T1  = 3.0122 Angstrom