Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_161-2_1_54_JYuPCV.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.9220 Angstrom
T1  -- O2  = 1.9220 Angstrom
T1  -- O1  = 1.9657 Angstrom
T1  -- O2  = 1.6102 Angstrom
T1  -- O1  = 1.9190 Angstrom
      mean = 1.8678 Angstrom

        T-O SUMMARY
          Range  = 1.6102 A <--> 1.9657 A
          Mean   = 1.8678 A
          StdDev = 0.1322 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O2  =  83.778 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  = 120.941 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 138.033 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  = 117.056 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  =  76.411 deg; O2  -- O1  = 2 A
O2  -- T1  -- O2  = 138.028 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  =  81.698 deg; O2  -- O1  = 3 A
O1  -- T1  -- O2  =  76.839 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  = 114.194 deg; O1  -- O1  = 3 A
O2  -- T1  -- O1  =  80.516 deg; O2  -- O1  = 2 A
       76.411 deg <-- 102.750 deg --> 138.033 deg

        O-T-O SUMMARY
          Range  = 76.4114 deg <--> 138.0331 deg
          Mean   = 102.7496 deg
          StdDev = 24.3254 deg

        O--O SUMMARY
          Range  = 2.2395 A <--> 3.3827 A
          Mean   = 2.8536 A
          StdDev = 0.4638 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 166.961 deg ; T1  -- T1   3.8596 A

T1  -- O2  -- T1  = 130.763 deg ; T1  -- T1   3.4946 A
T1  -- O2  -- T1  = 112.355 deg ; T1  -- T1   2.9395 A
T1  -- O2  -- T1  = 112.354 deg ; T1  -- T1   2.9396 A


        T-O-T SUMMARY
          Range  = 112.3536° <--> 166.9608 deg
          Mean   = 130.6081 deg
          StdDev = 22.7726 deg

        T--T SUMMARY
          Range  = 2.9395 A <--> 3.8596 A
          Mean   = 3.3083 A
          StdDev = 0.3991 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2928 A
O1  -- O2  = 2.2395 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.4946 Angstrom
  T1  -- T1  = 3.4946 Angstrom
  T1  -- T1  = 2.9395 Angstrom
  T1  -- T1  = 2.9396 Angstrom
  T1  -- T1  = 2.9395 Angstrom
  T1  -- T1  = 2.9396 Angstrom