Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_160-2_2_505_zeTHja.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 21.84 T-atoms per nm^3
Material density = 2.180 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O3  = 1.6299 Angstrom
T1  -- O4  = 1.6057 Angstrom
T1  -- O2  = 1.5768 Angstrom
T1  -- O1  = 1.6418 Angstrom
      mean = 1.6135 Angstrom
        t1 = 0.034202  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035885  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6422 Angstrom
T2  -- O3  = 1.6744 Angstrom
T2  -- O2  = 1.6644 Angstrom
T2  -- O4  = 1.6304 Angstrom
      mean = 1.6529 Angstrom
        t1 = 0.049020  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031031  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5768 A <--> 1.6744 A
          Mean   = 1.6332 A
          StdDev = 0.0294 A

       t1 Range  = 0.0342 <-- 0.0416 --> 0.0490
       t2 Range  = 0.0310 <-- 0.0335 --> 0.0359

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O3  -- T1  -- O4  = 104.695 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 103.232 deg; O3  -- O2  = 3 A
O3  -- T1  -- O1  = 117.212 deg; O3  -- O1  = 3 A
O4  -- T1  -- O2  = 115.415 deg; O4  -- O2  = 3 A
O4  -- T1  -- O1  = 107.635 deg; O4  -- O1  = 3 A
O2  -- T1  -- O1  = 108.914 deg; O2  -- O1  = 3 A
       103.232 deg <-- 109.517 deg --> 117.212 deg

O5  -- T2  -- O3  = 104.264 deg; O5  -- O3  = 3 A
O5  -- T2  -- O2  = 113.739 deg; O5  -- O2  = 3 A
O5  -- T2  -- O4  = 106.098 deg; O5  -- O4  = 3 A
O3  -- T2  -- O2  = 111.457 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 120.279 deg; O3  -- O4  = 3 A
O2  -- T2  -- O4  = 101.282 deg; O2  -- O4  = 3 A
       101.282 deg <-- 109.520 deg --> 120.279 deg

        O-T-O SUMMARY
          Range  = 101.2815 deg <--> 120.2791 deg
          Mean   = 109.5187 deg
          StdDev = 5.8515 deg

        O--O SUMMARY
          Range  = 2.5138 A <--> 2.8662 A
          Mean   = 2.6646 A
          StdDev = 0.1061 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O3  - T1  - O4  - T2  =  94.699 deg; T2  -- T2  = 4.4403 A
T2  - O3  - T1  - O2  - T1  = 120.713 deg; T2  -- T1  = 5.0484 A
T2  - O3  - T1  - O1  - T2  = 104.856 deg; T2  -- T2  = 4.7263 A
T2  - O4  - T1  - O2  - T1  =  91.905 deg; T2  -- T1  = 4.1994 A
T2  - O4  - T1  - O1  - T2  = 120.806 deg; T2  -- T2  = 5.2118 A
T1  - O2  - T1  - O1  - T2  = 121.213 deg; T1  -- T2  = 5.0227 A

T2  - O5  - T2  - O3  - T1  = 122.997 deg; T2  -- T1  = 5.2428 A
T2  - O5  - T2  - O2  - T1  =  88.095 deg; T2  -- T1  = 4.1994 A
T2  - O5  - T2  - O4  - T1  = 122.461 deg; T2  -- T1  = 5.2675 A
T1  - O3  - T2  - O2  - T1  = 120.231 deg; T1  -- T1  = 5.1968 A
T1  - O3  - T2  - O4  - T1  = 104.856 deg; T1  -- T1  = 4.7263 A
T1  - O2  - T2  - O4  - T1  =  94.209 deg; T1  -- T1  = 4.4228 A

        T-T-T SUMMARY
          Range  = 88.0955 deg <--> 122.9970 deg
          Mean   = 108.9202 deg
          StdDev = 13.3715 deg

        T--T SUMMARY
          Range  = 4.1994 A <--> 5.2675 A
          Mean   = 4.8087 A
          StdDev = 0.3960 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 117.309 deg ; T1  -- T1   2.8044 A

T1  -- O2  -- T2  = 135.794 deg ; T1  -- T2   3.0032 A

T1  -- O3  -- T2  = 127.203 deg ; T1  -- T2   2.9598 A

T1  -- O4  -- T2  = 139.276 deg ; T1  -- T2   3.0339 A

T2  -- O5  -- T2  = 132.476 deg ; T2  -- T2   3.0061 A


        T-O-T SUMMARY
          Range  = 117.3087° <--> 139.2765 deg
          Mean   = 130.4115 deg
          StdDev = 7.7965 deg

        T--T SUMMARY
          Range  = 2.8044 A <--> 3.0339 A
          Mean   = 2.9615 A
          StdDev = 0.0834 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

<TD10> = 894.000
Average ring size = 5.7143