Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_160-2_2_449_bE7L1h.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 19.14 T-atoms per nm^3
Material density = 1.910 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6205 Angstrom
T1  -- O3  = 1.6222 Angstrom
T1  -- O4  = 1.6218 Angstrom
T1  -- O1  = 1.6209 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.007089  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000622  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6219 Angstrom
T2  -- O5  = 1.6207 Angstrom
T2  -- O6  = 1.6215 Angstrom
T2  -- O4  = 1.6215 Angstrom
      mean = 1.6214 Angstrom
        t1 = 0.007089  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000192  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6205 A <--> 1.6222 A
          Mean   = 1.6214 A
          StdDev = 0.0006 A

       t1 Range  = 0.0071 <-- 0.0071 --> 0.0071
       t2 Range  = 0.0002 <-- 0.0004 --> 0.0006

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 109.465 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.396 deg; O2  -- O4  = 3 A
O2  -- T1  -- O1  = 109.538 deg; O2  -- O1  = 3 A
O3  -- T1  -- O4  = 109.529 deg; O3  -- O4  = 3 A
O3  -- T1  -- O1  = 109.628 deg; O3  -- O1  = 3 A
O4  -- T1  -- O1  = 109.270 deg; O4  -- O1  = 3 A
       109.270 deg <-- 109.471 deg --> 109.628 deg

O3  -- T2  -- O5  = 109.498 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.468 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.478 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.430 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.464 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.489 deg; O6  -- O4  = 3 A
       109.430 deg <-- 109.471 deg --> 109.498 deg

        O-T-O SUMMARY
          Range  = 109.2701 deg <--> 109.6284 deg
          Mean   = 109.4701 deg
          StdDev = 0.0850 deg

        O--O SUMMARY
          Range  = 2.6444 A <--> 2.6506 A
          Mean   = 2.6477 A
          StdDev = 0.0016 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T2  =  89.835 deg; T1  -- T2  = 4.2787 A
T1  - O2  - T1  - O4  - T1  = 120.000 deg; T1  -- T1  = 5.2564 A
T1  - O2  - T1  - O1  - T2  = 119.711 deg; T1  -- T2  = 5.2350 A
T2  - O3  - T1  - O4  - T1  = 119.703 deg; T2  -- T1  = 5.2355 A
T2  - O3  - T1  - O1  - T2  = 120.685 deg; T2  -- T2  = 5.2475 A
T1  - O4  - T1  - O1  - T2  =  90.078 deg; T1  -- T2  = 4.2798 A

T1  - O3  - T2  - O5  - T2  =  90.165 deg; T1  -- T2  = 4.2787 A
T1  - O3  - T2  - O6  - T2  = 119.513 deg; T1  -- T2  = 5.2375 A
T1  - O3  - T2  - O4  - T1  = 120.585 deg; T1  -- T1  = 5.2449 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.2485 A
T2  - O5  - T2  - O4  - T1  = 119.801 deg; T2  -- T1  = 5.2223 A
T2  - O6  - T2  - O4  - T1  =  89.922 deg; T2  -- T1  = 4.2798 A

        T-T-T SUMMARY
          Range  = 89.8350 deg <--> 120.6854 deg
          Mean   = 109.1039 deg
          StdDev = 14.5559 deg

        T--T SUMMARY
          Range  = 4.2787 A <--> 5.2564 A
          Mean   = 4.8912 A
          StdDev = 0.4662 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 138.561 deg ; T1  -- T1   3.0322 A

T1  -- O2  -- T1  = 139.175 deg ; T1  -- T1   3.0374 A

T1  -- O3  -- T2  = 137.381 deg ; T1  -- T2   3.0223 A

T1  -- O4  -- T2  = 136.865 deg ; T1  -- T2   3.0162 A

T2  -- O5  -- T2  = 137.409 deg ; T2  -- T2   3.0200 A

T2  -- O6  -- T2  = 139.276 deg ; T2  -- T2   3.0404 A


        T-O-T SUMMARY
          Range  = 136.8650° <--> 139.2760 deg
          Mean   = 138.1112 deg
          StdDev = 0.9505 deg

        T--T SUMMARY
          Range  = 3.0162 A <--> 3.0404 A
          Mean   = 3.0281 A
          StdDev = 0.0092 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 791.000
Average ring size = 5.1429