Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_80542_VJmhuu.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.27 T-atoms per nm^3
Material density = 1.923 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6153 Angstrom
T1  -- O2  = 1.6159 Angstrom
T1  -- O3  = 1.6096 Angstrom
T1  -- O4  = 1.6195 Angstrom
      mean = 1.6150 Angstrom
        t1 = 0.003292  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001018  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6097 Angstrom
T2  -- O5  = 1.6159 Angstrom
T2  -- O6  = 1.6154 Angstrom
T2  -- O4  = 1.6196 Angstrom
      mean = 1.6151 Angstrom
        t1 = 0.003389  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001305  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6096 A <--> 1.6196 A
          Mean   = 1.6151 A
          StdDev = 0.0036 A

       t1 Range  = 0.0033 <-- 0.0033 --> 0.0034
       t2 Range  = 0.0010 <-- 0.0012 --> 0.0013

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.356 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.532 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.373 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.515 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.441 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.609 deg; O3  -- O4  = 3 A
       109.356 deg <-- 109.471 deg --> 109.609 deg

O3  -- T2  -- O5  = 109.525 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.454 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.567 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.477 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.474 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.330 deg; O6  -- O4  = 3 A
       109.330 deg <-- 109.471 deg --> 109.567 deg

        O-T-O SUMMARY
          Range  = 109.3297 deg <--> 109.6094 deg
          Mean   = 109.4761 deg
          StdDev = 0.0825 deg

        O--O SUMMARY
          Range  = 2.6330 A <--> 2.6419 A
          Mean   = 2.6374 A
          StdDev = 0.0029 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 109.588 deg; T2  -- T1  = 5.2710 A
T2  - O1  - T1  - O3  - T1  = 109.562 deg; T2  -- T1  = 5.2691 A
T2  - O1  - T1  - O4  - T2  =  90.020 deg; T2  -- T2  = 4.4379 A
T1  - O2  - T1  - O3  - T1  = 109.440 deg; T1  -- T1  = 5.2753 A
T1  - O2  - T1  - O4  - T2  = 118.040 deg; T1  -- T2  = 5.3894 A
T1  - O3  - T1  - O4  - T2  = 118.074 deg; T1  -- T2  = 5.3894 A

T1  - O3  - T2  - O5  - T2  = 109.554 deg; T1  -- T2  = 5.2700 A
T1  - O3  - T2  - O6  - T2  = 109.527 deg; T1  -- T2  = 5.2682 A
T1  - O3  - T2  - O4  - T1  =  89.980 deg; T1  -- T1  = 4.4363 A
T2  - O5  - T2  - O6  - T2  = 109.442 deg; T2  -- T2  = 5.2758 A
T2  - O5  - T2  - O4  - T1  = 118.096 deg; T2  -- T1  = 5.3912 A
T2  - O6  - T2  - O4  - T1  = 118.099 deg; T2  -- T1  = 5.3903 A

        T-T-T SUMMARY
          Range  = 89.9796 deg <--> 118.0987 deg
          Mean   = 109.0824 deg
          StdDev = 9.8395 deg

        T--T SUMMARY
          Range  = 4.4363 A <--> 5.3912 A
          Mean   = 5.1628 A
          StdDev = 0.3482 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 179.805 deg ; T1  -- T1   3.2305 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2317 A

T1  -- O3  -- T2  = 179.789 deg ; T1  -- T2   3.2192 A

T1  -- O4  -- T2  = 141.028 deg ; T1  -- T2   3.0536 A

T2  -- O5  -- T2  = 179.918 deg ; T2  -- T2   3.2319 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2307 A


        T-O-T SUMMARY
          Range  = 141.0280° <--> 180.0000 deg
          Mean   = 173.4233 deg
          StdDev = 14.6412 deg

        T--T SUMMARY
          Range  = 3.0536 A <--> 3.2319 A
          Mean   = 3.1996 A
          StdDev = 0.0661 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000