Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_201659_bvyaHc.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 28.88 T-atoms per nm^3
Material density = 2.882 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6572 Angstrom
T1  -- O2  = 1.6654 Angstrom
T1  -- O3  = 1.6478 Angstrom
T1  -- O1  = 1.6500 Angstrom
      mean = 1.6551 Angstrom
        t1 = 0.077564  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049394  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6468 Angstrom
T2  -- O2  = 1.6468 Angstrom
T2  -- O3  = 1.6331 Angstrom
T2  -- O3  = 1.6331 Angstrom
      mean = 1.6400 Angstrom
        t1 = 0.079988  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.083437  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6331 A <--> 1.6654 A
          Mean   = 1.6501 A
          StdDev = 0.0100 A

       t1 Range  = 0.0776 <-- 0.0788 --> 0.0800
       t2 Range  = 0.0494 <-- 0.0664 --> 0.0834

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 100.536 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.372 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 127.849 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 126.704 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  =  99.992 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 100.500 deg; O3  -- O1  = 3 A
       99.992 deg <-- 109.992 deg --> 127.849 deg

O2  -- T2  -- O2  = 104.890 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 128.554 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 100.187 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 100.187 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 128.554 deg; O2  -- O3  = 3 A
O3  -- T2  -- O3  =  97.956 deg; O3  -- O3  = 2 A
       97.956 deg <-- 110.055 deg --> 128.554 deg

        O-T-O SUMMARY
          Range  = 97.9563 deg <--> 128.5541 deg
          Mean   = 110.0234 deg
          StdDev = 12.8523 deg

        O--O SUMMARY
          Range  = 2.4643 A <--> 2.9705 A
          Mean   = 2.6825 A
          StdDev = 0.2012 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 119.398 deg; T2  -- T1  = 5.4052 A
T2  - O1  - T1  - O3  - T1  =  91.811 deg; T2  -- T1  = 4.4962 A
T2  - O1  - T1  - O1  - T2  = 143.256 deg; T2  -- T2  = 5.9159 A
T1  - O2  - T1  - O3  - T1  = 143.016 deg; T1  -- T1  = 5.9411 A
T1  - O2  - T1  - O1  - T2  =  91.209 deg; T1  -- T2  = 4.4570 A
T1  - O3  - T1  - O1  - T2  =  70.032 deg; T1  -- T2  = 3.5793 A

T1  - O2  - T2  - O2  - T1  = 143.256 deg; T1  -- T1  = 5.9159 A
T1  - O2  - T2  - O3  - T1  =  69.098 deg; T1  -- T1  = 3.5481 A
T1  - O2  - T2  - O3  - T1  =  91.759 deg; T1  -- T1  = 4.4750 A
T1  - O2  - T2  - O3  - T1  =  91.759 deg; T1  -- T1  = 4.4750 A
T1  - O2  - T2  - O3  - T1  = 119.327 deg; T1  -- T1  = 5.3604 A
T1  - O3  - T2  - O3  - T1  = 143.256 deg; T1  -- T1  = 5.9159 A

        T-T-T SUMMARY
          Range  = 69.0980 deg <--> 143.2562 deg
          Mean   = 109.7647 deg
          StdDev = 27.8379 deg

        T--T SUMMARY
          Range  = 3.5481 A <--> 5.9411 A
          Mean   = 4.9571 A
          StdDev = 0.8658 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 142.567 deg ; T1  -- T1   3.1323 A

T1  -- O2  -- T2  = 141.625 deg ; T1  -- T2   3.1282 A

T1  -- O3  -- T2  = 142.342 deg ; T1  -- T2   3.1054 A


        T-O-T SUMMARY
          Range  = 141.6249° <--> 142.5674 deg
          Mean   = 142.1783 deg
          StdDev = 0.4105 deg

        T--T SUMMARY
          Range  = 3.1054 A <--> 3.1323 A
          Mean   = 3.1220 A
          StdDev = 0.0121 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

<TD10> = 1169.000
Average ring size = 6.5455