Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_199900_8DswQV.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 17.89 T-atoms per nm^3
Material density = 1.785 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6132 Angstrom
T1  -- O2  = 1.6255 Angstrom
T1  -- O2  = 1.6239 Angstrom
T1  -- O3  = 1.6514 Angstrom
      mean = 1.6285 Angstrom
        t1 = 0.014270  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006184  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6240 Angstrom
T2  -- O3  = 1.6240 Angstrom
T2  -- O4  = 1.5834 Angstrom
T2  -- O4  = 1.5834 Angstrom
      mean = 1.6037 Angstrom
        t1 = 0.033466  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021956  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5834 A <--> 1.6514 A
          Mean   = 1.6202 A
          StdDev = 0.0204 A

       t1 Range  = 0.0143 <-- 0.0239 --> 0.0335
       t2 Range  = 0.0062 <-- 0.0141 --> 0.0220

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.555 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.645 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.499 deg; O1  -- O3  = 3 A
O2  -- T1  -- O2  = 108.180 deg; O2  -- O2  = 3 A
O2  -- T1  -- O3  = 111.072 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 108.863 deg; O2  -- O3  = 3 A
       108.180 deg <-- 109.469 deg --> 111.072 deg

O3  -- T2  -- O3  = 119.659 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 107.742 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 105.735 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 105.735 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 107.742 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 110.083 deg; O4  -- O4  = 3 A
       105.735 deg <-- 109.450 deg --> 119.659 deg

        O-T-O SUMMARY
          Range  = 105.7354 deg <--> 119.6590 deg
          Mean   = 109.4323 deg
          StdDev = 3.5393 deg

        O--O SUMMARY
          Range  = 2.5572 A <--> 2.8081 A
          Mean   = 2.6398 A
          StdDev = 0.0683 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 118.239 deg; T1  -- T1  = 5.5127 A
T1  - O1  - T1  - O2  - T1  = 108.557 deg; T1  -- T1  = 5.1908 A
T1  - O1  - T1  - O3  - T2  =  91.788 deg; T1  -- T2  = 4.3510 A
T1  - O2  - T1  - O2  - T1  = 107.030 deg; T1  -- T1  = 5.1643 A
T1  - O2  - T1  - O3  - T2  = 138.307 deg; T1  -- T2  = 5.6835 A
T1  - O2  - T1  - O3  - T2  =  87.603 deg; T1  -- T2  = 4.1952 A

T1  - O3  - T2  - O3  - T2  =  92.411 deg; T1  -- T2  = 4.3510 A
T1  - O3  - T2  - O4  - T1  = 178.957 deg; T1  -- T1  = 5.7069 A
T1  - O3  - T2  - O4  - T2  =  88.187 deg; T1  -- T2  = 4.1952 A
T2  - O3  - T2  - O4  - T1  =  88.187 deg; T2  -- T1  = 4.1952 A
T2  - O3  - T2  - O4  - T2  = 110.083 deg; T2  -- T2  = 5.1908 A
T1  - O4  - T2  - O4  - T2  =  92.411 deg; T1  -- T2  = 4.3511 A

        T-T-T SUMMARY
          Range  = 87.6032 deg <--> 178.9571 deg
          Mean   = 109.1787 deg
          StdDev = 26.3141 deg

        T--T SUMMARY
          Range  = 4.1952 A <--> 5.7069 A
          Mean   = 4.8619 A
          StdDev = 0.6008 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2264 A

T1  -- O2  -- T1  = 159.356 deg ; T1  -- T1   3.1968 A

T1  -- O3  -- T2  = 121.196 deg ; T1  -- T2   2.8536 A

T2  -- O4  -- T2  = 180.000 deg ; T2  -- T2   3.1668 A


        T-O-T SUMMARY
          Range  = 121.1961° <--> 180.0000 deg
          Mean   = 157.3006 deg
          StdDev = 24.8292 deg

        T--T SUMMARY
          Range  = 2.8536 A <--> 3.2264 A
          Mean   = 3.1029 A
          StdDev = 0.1617 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 33 51 72 96 126 160 196 235 281 331 382 436 498
TD10 = 768
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{2}
Weight = 26

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 8 16 30 48 66 92 128 158 182 230 294 330 354 430 528
TD10 = 733
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.10_{2}.*
Weight = 21

<TD10> = 756.333
Average ring size = 5.5556