Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_196709_TRhyo2.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 30.41 T-atoms per nm^3
Material density = 3.034 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6343 Angstrom
T1  -- O1  = 1.6289 Angstrom
T1  -- O3  = 1.5351 Angstrom
T1  -- O2  = 1.6218 Angstrom
      mean = 1.6050 Angstrom
        t1 = 0.069297  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.044011  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6157 Angstrom
T2  -- O2  = 1.6157 Angstrom
T2  -- O3  = 1.7037 Angstrom
T2  -- O3  = 1.7037 Angstrom
      mean = 1.6597 Angstrom
        t1 = 0.081495  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048942  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5351 A <--> 1.7037 A
          Mean   = 1.6232 A
          StdDev = 0.0496 A

       t1 Range  = 0.0693 <-- 0.0754 --> 0.0815
       t2 Range  = 0.0440 <-- 0.0465 --> 0.0489

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 112.303 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 109.551 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 113.058 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  95.360 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 123.336 deg; O1  -- O2  = 3 A
O3  -- T1  -- O2  =  99.736 deg; O3  -- O2  = 2 A
       95.360 deg <-- 108.891 deg --> 123.336 deg

O2  -- T2  -- O2  = 108.762 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 106.039 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 100.151 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 100.151 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 106.039 deg; O2  -- O3  = 3 A
O3  -- T2  -- O3  = 134.274 deg; O3  -- O3  = 3 A
       100.151 deg <-- 109.236 deg --> 134.274 deg

        O-T-O SUMMARY
          Range  = 95.3596 deg <--> 134.2745 deg
          Mean   = 109.0635 deg
          StdDev = 10.5352 deg

        O--O SUMMARY
          Range  = 2.3403 A <--> 3.1396 A
          Mean   = 2.6496 A
          StdDev = 0.1989 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  = 104.511 deg; T1  -- T1  = 4.5349 A
T1  - O1  - T1  - O3  - T2  = 155.665 deg; T1  -- T2  = 5.9572 A
T1  - O1  - T1  - O2  - T2  = 106.211 deg; T1  -- T2  = 4.6217 A
T1  - O1  - T1  - O3  - T2  =  90.555 deg; T1  -- T2  = 4.3370 A
T1  - O1  - T1  - O2  - T2  = 107.613 deg; T1  -- T2  = 4.6638 A
T2  - O3  - T1  - O2  - T2  =  86.674 deg; T2  -- T2  = 4.2183 A

T1  - O2  - T2  - O2  - T1  = 110.499 deg; T1  -- T1  = 5.3014 A
T1  - O2  - T2  - O3  - T1  =  85.705 deg; T1  -- T1  = 4.1806 A
T1  - O2  - T2  - O3  - T1  =  93.326 deg; T1  -- T1  = 4.4693 A
T1  - O2  - T2  - O3  - T1  =  93.326 deg; T1  -- T1  = 4.4693 A
T1  - O2  - T2  - O3  - T1  =  85.705 deg; T1  -- T1  = 4.1806 A
T1  - O3  - T2  - O3  - T1  = 178.304 deg; T1  -- T1  = 5.8223 A

        T-T-T SUMMARY
          Range  = 85.7050 deg <--> 178.3043 deg
          Mean   = 108.1745 deg
          StdDev = 28.1648 deg

        T--T SUMMARY
          Range  = 4.1806 A <--> 5.9572 A
          Mean   = 4.7297 A
          StdDev = 0.5972 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 122.976 deg ; T1  -- T1   2.8675 A

T1  -- O2  -- T2  = 170.414 deg ; T1  -- T2   3.2261 A

T1  -- O3  -- T2  = 127.962 deg ; T1  -- T2   2.9115 A


        T-O-T SUMMARY
          Range  = 122.9765° <--> 170.4144 deg
          Mean   = 140.4511 deg
          StdDev = 21.7426 deg

        T--T SUMMARY
          Range  = 2.8675 A <--> 3.2261 A
          Mean   = 3.0017 A
          StdDev = 0.1631 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 25
Vertex symbol  = 4.8_{6}.6.6.6.6
Weight = 25

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 40 64 90 120 160 200 244 300 354 412 484 552 624
TD10 = 957
Circuit symbol = 4.4.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 29
Vertex symbol  = 4.4.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 29

<TD10> = 958.333
Average ring size = 6.4000