Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_196706_hfBl4C.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 28.92 T-atoms per nm^3
Material density = 2.885 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6391 Angstrom
T1  -- O2  = 1.6044 Angstrom
T1  -- O3  = 1.5699 Angstrom
T1  -- O1  = 1.6429 Angstrom
      mean = 1.6141 Angstrom
        t1 = 0.034598  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038660  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6177 Angstrom
T2  -- O2  = 1.6177 Angstrom
T2  -- O3  = 1.6426 Angstrom
T2  -- O3  = 1.6426 Angstrom
      mean = 1.6302 Angstrom
        t1 = 0.176430  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.131729  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5699 A <--> 1.6429 A
          Mean   = 1.6195 A
          StdDev = 0.0266 A

       t1 Range  = 0.0346 <-- 0.1055 --> 0.1764
       t2 Range  = 0.0387 <-- 0.0852 --> 0.1317

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.048 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 102.373 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 111.178 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 104.826 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.965 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 114.202 deg; O3  -- O1  = 3 A
       102.373 deg <-- 109.432 deg --> 114.202 deg

O2  -- T2  -- O2  = 125.769 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  =  81.619 deg; O2  -- O3  = 2 A
O2  -- T2  -- O3  =  81.567 deg; O2  -- O3  = 2 A
O2  -- T2  -- O3  =  81.567 deg; O2  -- O3  = 2 A
O2  -- T2  -- O3  =  81.619 deg; O2  -- O3  = 2 A
O3  -- T2  -- O3  = 142.581 deg; O3  -- O3  = 3 A
       81.567 deg <-- 99.120 deg --> 142.581 deg

        O-T-O SUMMARY
          Range  = 81.5666 deg <--> 142.5805 deg
          Mean   = 104.2762 deg
          StdDev = 18.9519 deg

        O--O SUMMARY
          Range  = 2.1297 A <--> 3.1116 A
          Mean   = 2.5263 A
          StdDev = 0.3197 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  83.289 deg; T1  -- T2  = 4.0194 A
T1  - O1  - T1  - O3  - T1  = 101.488 deg; T1  -- T1  = 4.5069 A
T1  - O1  - T1  - O1  - T2  = 145.386 deg; T1  -- T2  = 5.8027 A
T2  - O2  - T1  - O3  - T1  = 128.143 deg; T2  -- T1  = 5.4360 A
T2  - O2  - T1  - O1  - T2  = 103.595 deg; T2  -- T2  = 4.9511 A
T1  - O3  - T1  - O1  - T2  = 100.349 deg; T1  -- T2  = 4.6703 A

T1  - O2  - T2  - O2  - T1  = 130.907 deg; T1  -- T1  = 5.7619 A
T1  - O2  - T2  - O3  - T1  =  76.405 deg; T1  -- T1  = 3.8965 A
T1  - O2  - T2  - O3  - T1  =  80.851 deg; T1  -- T1  = 4.0857 A
T1  - O2  - T2  - O3  - T1  =  80.851 deg; T1  -- T1  = 4.0857 A
T1  - O2  - T2  - O3  - T1  =  76.405 deg; T1  -- T1  = 3.8965 A
T1  - O3  - T2  - O3  - T1  = 123.376 deg; T1  -- T1  = 5.5169 A

        T-T-T SUMMARY
          Range  = 76.4051 deg <--> 145.3863 deg
          Mean   = 102.5871 deg
          StdDev = 23.2417 deg

        T--T SUMMARY
          Range  = 3.8965 A <--> 5.8027 A
          Mean   = 4.7191 A
          StdDev = 0.7202 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 124.923 deg ; T1  -- T1   2.9102 A

T1  -- O2  -- T2  = 158.805 deg ; T1  -- T2   3.1672 A

T1  -- O3  -- T2  = 154.482 deg ; T1  -- T2   3.1333 A


        T-O-T SUMMARY
          Range  = 124.9233° <--> 158.8050 deg
          Mean   = 146.0699 deg
          StdDev = 15.3806 deg

        T--T SUMMARY
          Range  = 2.9102 A <--> 3.1672 A
          Mean   = 3.0702 A
          StdDev = 0.1164 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 2.1309 A
O2  -- O3  = 2.1297 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 474 546 610
TD10 = 959
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 25
Vertex symbol  = 4.8_{6}.6.6.6.6
Weight = 25

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 40 64 90 120 160 200 244 300 354 412 484 546 600
TD10 = 957
Circuit symbol = 4.4.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 29
Vertex symbol  = 4.4.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 29

<TD10> = 958.333
Average ring size = 6.4000