Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_196703_jc5Rd6.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 24.44 T-atoms per nm^3
Material density = 2.438 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6192 Angstrom
T1  -- O1  = 1.6197 Angstrom
T1  -- O2  = 1.6245 Angstrom
T1  -- O3  = 1.6250 Angstrom
      mean = 1.6221 Angstrom
        t1 = 0.007997  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002706  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6229 Angstrom
T2  -- O3  = 1.6229 Angstrom
T2  -- O2  = 1.6226 Angstrom
T2  -- O2  = 1.6226 Angstrom
      mean = 1.6228 Angstrom
        t1 = 0.008915  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003530  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6192 A <--> 1.6250 A
          Mean   = 1.6224 A
          StdDev = 0.0022 A

       t1 Range  = 0.0080 <-- 0.0085 --> 0.0089
       t2 Range  = 0.0027 <-- 0.0031 --> 0.0035

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 109.501 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 110.034 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.960 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 108.942 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.965 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.416 deg; O2  -- O3  = 3 A
       108.942 deg <-- 109.470 deg --> 110.034 deg

O3  -- T2  -- O3  = 110.434 deg; O3  -- O3  = 3 A
O3  -- T2  -- O2  = 108.850 deg; O3  -- O2  = 3 A
O3  -- T2  -- O2  = 109.187 deg; O3  -- O2  = 3 A
O3  -- T2  -- O2  = 109.187 deg; O3  -- O2  = 3 A
O3  -- T2  -- O2  = 108.850 deg; O3  -- O2  = 3 A
O2  -- T2  -- O2  = 110.328 deg; O2  -- O2  = 3 A
       108.850 deg <-- 109.473 deg --> 110.434 deg

        O-T-O SUMMARY
          Range  = 108.8501 deg <--> 110.4341 deg
          Mean   = 109.4710 deg
          StdDev = 0.5574 deg

        O--O SUMMARY
          Range  = 2.6398 A <--> 2.6659 A
          Mean   = 2.6494 A
          StdDev = 0.0092 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T2  = 100.401 deg; T1  -- T2  = 4.6378 A
T1  - O1  - T1  - O2  - T1  = 109.506 deg; T1  -- T1  = 4.9862 A
T1  - O1  - T1  - O3  - T2  = 100.567 deg; T1  -- T2  = 4.6431 A
T2  - O1  - T1  - O2  - T1  = 121.653 deg; T2  -- T1  = 5.2707 A
T2  - O1  - T1  - O3  - T2  =  99.102 deg; T2  -- T2  = 4.5405 A
T1  - O2  - T1  - O3  - T2  = 121.849 deg; T1  -- T2  = 5.2753 A

T1  - O3  - T2  - O3  - T1  = 104.303 deg; T1  -- T1  = 4.7114 A
T1  - O3  - T2  - O2  - T1  =  80.898 deg; T1  -- T1  = 3.8710 A
T1  - O3  - T2  - O2  - T1  = 155.663 deg; T1  -- T1  = 5.8322 A
T1  - O3  - T2  - O2  - T1  = 155.666 deg; T1  -- T1  = 5.8330 A
T1  - O3  - T2  - O2  - T1  =  80.898 deg; T1  -- T1  = 3.8710 A
T1  - O2  - T2  - O2  - T1  = 104.303 deg; T1  -- T1  = 4.7114 A

        T-T-T SUMMARY
          Range  = 80.8979 deg <--> 155.6660 deg
          Mean   = 111.2340 deg
          StdDev = 23.3730 deg

        T--T SUMMARY
          Range  = 3.8710 A <--> 5.8330 A
          Mean   = 4.8486 A
          StdDev = 0.6119 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.954 deg ; T1  -- T1   3.0527 A

T1  -- O2  -- T2  = 133.504 deg ; T1  -- T2   2.9835 A

T1  -- O3  -- T2  = 133.401 deg ; T1  -- T2   2.9831 A


        T-O-T SUMMARY
          Range  = 133.4009° <--> 140.9541 deg
          Mean   = 135.9530 deg
          StdDev = 3.6127 deg

        T--T SUMMARY
          Range  = 2.9831 A <--> 3.0527 A
          Mean   = 3.0065 A
          StdDev = 0.0334 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 25
Vertex symbol  = 4.8_{6}.6.6.6.6
Weight = 25

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 40 64 90 120 160 200 244 300 354 412 484 552 624
TD10 = 957
Circuit symbol = 4.4.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 29
Vertex symbol  = 4.4.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 29

<TD10> = 958.333
Average ring size = 6.4000