Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_196699_m_zgEv.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 32.92 T-atoms per nm^3
Material density = 3.284 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6235 Angstrom
T1  -- O1  = 1.6179 Angstrom
T1  -- O2  = 1.6635 Angstrom
T1  -- O3  = 1.6555 Angstrom
      mean = 1.6401 Angstrom
        t1 = 0.044667  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032515  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6258 Angstrom
T2  -- O2  = 1.6258 Angstrom
T2  -- O3  = 1.6218 Angstrom
T2  -- O3  = 1.6218 Angstrom
      mean = 1.6238 Angstrom
        t1 = 0.179935  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.126884  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6179 A <--> 1.6635 A
          Mean   = 1.6347 A
          StdDev = 0.0181 A

       t1 Range  = 0.0447 <-- 0.1123 --> 0.1799
       t2 Range  = 0.0325 <-- 0.0797 --> 0.1269

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  99.752 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 113.986 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.336 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 106.895 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.913 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 115.903 deg; O2  -- O3  = 3 A
       99.752 deg <-- 109.298 deg --> 115.903 deg

O2  -- T2  -- O2  = 133.414 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  =  83.063 deg; O2  -- O3  = 2 A
O2  -- T2  -- O3  =  78.886 deg; O2  -- O3  = 2 A
O2  -- T2  -- O3  =  78.886 deg; O2  -- O3  = 2 A
O2  -- T2  -- O3  =  83.063 deg; O2  -- O3  = 2 A
O3  -- T2  -- O3  = 133.286 deg; O3  -- O3  = 3 A
       78.886 deg <-- 98.433 deg --> 133.414 deg

        O-T-O SUMMARY
          Range  = 78.8857 deg <--> 133.4138 deg
          Mean   = 103.8652 deg
          StdDev = 18.8368 deg

        O--O SUMMARY
          Range  = 2.0632 A <--> 2.9865 A
          Mean   = 2.5362 A
          StdDev = 0.3337 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T2  = 100.939 deg; T1  -- T2  = 4.6668 A
T1  - O1  - T1  - O2  - T2  = 129.688 deg; T1  -- T2  = 5.4858 A
T1  - O1  - T1  - O3  - T1  =  85.690 deg; T1  -- T1  = 3.8747 A
T2  - O1  - T1  - O2  - T2  = 108.837 deg; T2  -- T2  = 5.2085 A
T2  - O1  - T1  - O3  - T1  = 150.709 deg; T2  -- T1  = 5.8482 A
T2  - O2  - T1  - O3  - T1  =  87.248 deg; T2  -- T1  = 4.1879 A

T1  - O2  - T2  - O2  - T1  =  71.163 deg; T1  -- T1  = 3.7264 A
T1  - O2  - T2  - O3  - T1  =  79.412 deg; T1  -- T1  = 4.0914 A
T1  - O2  - T2  - O3  - T1  = 119.356 deg; T1  -- T1  = 5.5406 A
T1  - O2  - T2  - O3  - T1  = 119.769 deg; T1  -- T1  = 5.5273 A
T1  - O2  - T2  - O3  - T1  =  79.412 deg; T1  -- T1  = 4.0914 A
T1  - O3  - T2  - O3  - T1  =  71.163 deg; T1  -- T1  = 3.7264 A

        T-T-T SUMMARY
          Range  = 71.1630 deg <--> 150.7089 deg
          Mean   = 100.2822 deg
          StdDev = 24.5799 deg

        T--T SUMMARY
          Range  = 3.7264 A <--> 5.8482 A
          Mean   = 4.6646 A
          StdDev = 0.7760 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 123.027 deg ; T1  -- T1   2.8490 A

T1  -- O2  -- T2  = 152.479 deg ; T1  -- T2   3.1949 A

T1  -- O3  -- T2  = 156.622 deg ; T1  -- T2   3.2093 A


        T-O-T SUMMARY
          Range  = 123.0273° <--> 156.6220 deg
          Mean   = 144.0426 deg
          StdDev = 15.2777 deg

        T--T SUMMARY
          Range  = 2.8490 A <--> 3.2093 A
          Mean   = 3.0844 A
          StdDev = 0.1702 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 2.1532 A
O2  -- O3  = 2.0632 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 474 546 610
TD10 = 959
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 25
Vertex symbol  = 4.8_{6}.6.6.6.6
Weight = 25

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 40 64 90 120 160 200 244 300 354 412 484 546 600
TD10 = 957
Circuit symbol = 4.4.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 29
Vertex symbol  = 4.4.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 29

<TD10> = 958.333
Average ring size = 6.4000