Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_183659_P_VCiC.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.10 T-atoms per nm^3
Material density = 1.905 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6159 Angstrom
T1  -- O2  = 1.6168 Angstrom
T1  -- O4  = 1.6219 Angstrom
T1  -- O3  = 1.6100 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.004300  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001906  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6185 Angstrom
T2  -- O3  = 1.6090 Angstrom
T2  -- O4  = 1.6224 Angstrom
T2  -- O5  = 1.6146 Angstrom
      mean = 1.6161 Angstrom
        t1 = 0.004414  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002291  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6090 A <--> 1.6224 A
          Mean   = 1.6161 A
          StdDev = 0.0046 A

       t1 Range  = 0.0043 <-- 0.0044 --> 0.0044
       t2 Range  = 0.0019 <-- 0.0021 --> 0.0023

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.451 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.566 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.131 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.302 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.874 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.503 deg; O4  -- O3  = 3 A
       109.131 deg <-- 109.471 deg --> 109.874 deg

O2  -- T2  -- O3  = 109.750 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.495 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.426 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.501 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.176 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.478 deg; O4  -- O5  = 3 A
       109.176 deg <-- 109.471 deg --> 109.750 deg

        O-T-O SUMMARY
          Range  = 109.1306 deg <--> 109.8742 deg
          Mean   = 109.4712 deg
          StdDev = 0.2022 deg

        O--O SUMMARY
          Range  = 2.6272 A <--> 2.6465 A
          Mean   = 2.6391 A
          StdDev = 0.0056 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 117.263 deg; T2  -- T1  = 5.3995 A
T2  - O1  - T1  - O4  - T2  = 119.236 deg; T2  -- T2  = 5.2791 A
T2  - O1  - T1  - O3  - T2  =  90.054 deg; T2  -- T2  = 4.4626 A
T1  - O2  - T1  - O4  - T2  = 119.381 deg; T1  -- T2  = 5.4051 A
T1  - O2  - T1  - O3  - T2  = 110.225 deg; T1  -- T2  = 5.2886 A
T2  - O4  - T1  - O3  - T2  =  89.994 deg; T2  -- T2  = 4.4165 A

T1  - O2  - T2  - O3  - T1  = 119.228 deg; T1  -- T1  = 5.2789 A
T1  - O2  - T2  - O4  - T1  =  89.946 deg; T1  -- T1  = 4.4584 A
T1  - O2  - T2  - O5  - T2  = 117.219 deg; T1  -- T2  = 5.3959 A
T1  - O3  - T2  - O4  - T1  =  90.006 deg; T1  -- T1  = 4.4170 A
T1  - O3  - T2  - O5  - T2  = 119.452 deg; T1  -- T2  = 5.4047 A
T1  - O4  - T2  - O5  - T2  = 110.268 deg; T1  -- T2  = 5.2877 A

        T-T-T SUMMARY
          Range  = 89.9464 deg <--> 119.4519 deg
          Mean   = 107.6892 deg
          StdDev = 12.9410 deg

        T--T SUMMARY
          Range  = 4.4165 A <--> 5.4051 A
          Mean   = 5.0412 A
          StdDev = 0.4312 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2319 A

T1  -- O2  -- T2  = 145.693 deg ; T1  -- T2   3.0914 A

T1  -- O3  -- T2  = 174.657 deg ; T1  -- T2   3.2155 A

T1  -- O4  -- T2  = 137.920 deg ; T1  -- T2   3.0279 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2291 A


        T-O-T SUMMARY
          Range  = 137.9201° <--> 180.0000 deg
          Mean   = 163.6541 deg
          StdDev = 18.3430 deg

        T--T SUMMARY
          Range  = 3.0279 A <--> 3.2319 A
          Mean   = 3.1592 A
          StdDev = 0.0849 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182