Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_183610_7V37UU.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.01 T-atoms per nm^3
Material density = 1.797 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6158 Angstrom
T1  -- O2  = 1.6108 Angstrom
T1  -- O4  = 1.6169 Angstrom
T1  -- O3  = 1.6168 Angstrom
      mean = 1.6151 Angstrom
        t1 = 0.004168  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001831  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6115 Angstrom
T2  -- O3  = 1.6161 Angstrom
T2  -- O5  = 1.6158 Angstrom
T2  -- O4  = 1.6167 Angstrom
      mean = 1.6150 Angstrom
        t1 = 0.003667  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001630  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6108 A <--> 1.6169 A
          Mean   = 1.6150 A
          StdDev = 0.0023 A

       t1 Range  = 0.0037 <-- 0.0039 --> 0.0042
       t2 Range  = 0.0016 <-- 0.0017 --> 0.0018

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.607 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.196 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 108.812 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 110.302 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 110.046 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 108.848 deg; O4  -- O3  = 3 A
       108.812 deg <-- 109.469 deg --> 110.302 deg

O2  -- T2  -- O3  = 110.064 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 109.329 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 109.964 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 109.227 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 109.207 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 109.029 deg; O5  -- O4  = 3 A
       109.029 deg <-- 109.470 deg --> 110.064 deg

        O-T-O SUMMARY
          Range  = 108.8124 deg <--> 110.3017 deg
          Mean   = 109.4693 deg
          StdDev = 0.4922 deg

        O--O SUMMARY
          Range  = 2.6286 A <--> 2.6488 A
          Mean   = 2.6373 A
          StdDev = 0.0063 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  89.995 deg; T2  -- T2  = 4.4555 A
T2  - O1  - T1  - O4  - T1  = 117.126 deg; T2  -- T1  = 5.4830 A
T2  - O1  - T1  - O3  - T2  =  90.152 deg; T2  -- T2  = 4.4582 A
T2  - O2  - T1  - O4  - T1  = 116.316 deg; T2  -- T1  = 5.3844 A
T2  - O2  - T1  - O3  - T2  = 117.725 deg; T2  -- T2  = 5.3131 A
T1  - O4  - T1  - O3  - T2  = 118.405 deg; T1  -- T2  = 5.4403 A

T1  - O2  - T2  - O3  - T1  =  90.005 deg; T1  -- T1  = 4.4559 A
T1  - O2  - T2  - O5  - T2  = 116.845 deg; T1  -- T2  = 5.4748 A
T1  - O2  - T2  - O4  - T1  =  89.848 deg; T1  -- T1  = 4.4464 A
T1  - O3  - T2  - O5  - T2  = 116.692 deg; T1  -- T2  = 5.3954 A
T1  - O3  - T2  - O4  - T1  = 117.698 deg; T1  -- T1  = 5.3124 A
T2  - O5  - T2  - O4  - T1  = 118.355 deg; T2  -- T1  = 5.4389 A

        T-T-T SUMMARY
          Range  = 89.8475 deg <--> 118.4049 deg
          Mean   = 108.2636 deg
          StdDev = 12.9958 deg

        T--T SUMMARY
          Range  = 4.4464 A <--> 5.4830 A
          Mean   = 5.0882 A
          StdDev = 0.4537 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2317 A

T1  -- O2  -- T2  = 164.958 deg ; T1  -- T2   3.1946 A

T1  -- O3  -- T2  = 147.814 deg ; T1  -- T2   3.1062 A

T1  -- O4  -- T2  = 147.112 deg ; T1  -- T2   3.1013 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2317 A


        T-O-T SUMMARY
          Range  = 147.1117° <--> 180.0000 deg
          Mean   = 163.9767 deg
          StdDev = 14.7465 deg

        T--T SUMMARY
          Range  = 3.1013 A <--> 3.2317 A
          Mean   = 3.1731 A
          StdDev = 0.0590 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182