Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_140762_SerORc.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.46 T-atoms per nm^3
Material density = 2.241 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6160 Angstrom
T1  -- O3  = 1.6225 Angstrom
T1  -- O4  = 1.6183 Angstrom
T1  -- O2  = 1.6217 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.006164  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000961  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6222 Angstrom
T2  -- O3  = 1.6231 Angstrom
T2  -- O4  = 1.6193 Angstrom
T2  -- O5  = 1.6158 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.006645  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002191  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6158 A <--> 1.6231 A
          Mean   = 1.6199 A
          StdDev = 0.0028 A

       t1 Range  = 0.0062 <-- 0.0064 --> 0.0066
       t2 Range  = 0.0010 <-- 0.0016 --> 0.0022

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.057 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.690 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.551 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.337 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.561 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.630 deg; O4  -- O2  = 3 A
       109.057 deg <-- 109.471 deg --> 109.690 deg

O2  -- T2  -- O3  = 109.443 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.966 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.250 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.974 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.577 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.613 deg; O4  -- O5  = 3 A
       108.966 deg <-- 109.471 deg --> 109.974 deg

        O-T-O SUMMARY
          Range  = 108.9664 deg <--> 109.9738 deg
          Mean   = 109.4708 deg
          StdDev = 0.2699 deg

        O--O SUMMARY
          Range  = 2.6375 A <--> 2.6556 A
          Mean   = 2.6452 A
          StdDev = 0.0050 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  = 107.519 deg; T2  -- T2  = 4.9036 A
T2  - O1  - T1  - O4  - T1  = 105.896 deg; T2  -- T1  = 4.9779 A
T2  - O1  - T1  - O2  - T2  = 109.018 deg; T2  -- T2  = 4.8939 A
T2  - O3  - T1  - O4  - T1  = 110.360 deg; T2  -- T1  = 5.1656 A
T2  - O3  - T1  - O2  - T2  = 107.852 deg; T2  -- T2  = 4.9036 A
T1  - O4  - T1  - O2  - T2  = 115.898 deg; T1  -- T2  = 5.2752 A

T1  - O2  - T2  - O3  - T1  = 109.018 deg; T1  -- T1  = 4.8939 A
T1  - O2  - T2  - O4  - T1  = 107.519 deg; T1  -- T1  = 4.9036 A
T1  - O2  - T2  - O5  - T2  = 116.141 deg; T1  -- T2  = 5.3000 A
T1  - O3  - T2  - O4  - T1  = 107.852 deg; T1  -- T1  = 4.9036 A
T1  - O3  - T2  - O5  - T2  = 104.472 deg; T1  -- T2  = 4.9274 A
T1  - O4  - T2  - O5  - T2  = 111.534 deg; T1  -- T2  = 5.2088 A

        T-T-T SUMMARY
          Range  = 104.4725 deg <--> 116.1409 deg
          Mean   = 109.4233 deg
          StdDev = 3.4562 deg

        T--T SUMMARY
          Range  = 4.8939 A <--> 5.3000 A
          Mean   = 5.0214 A
          StdDev = 0.1581 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 171.652 deg ; T1  -- T1   3.2234 A

T1  -- O2  -- T2  = 135.171 deg ; T1  -- T2   2.9988 A

T1  -- O3  -- T2  = 136.235 deg ; T1  -- T2   3.0118 A

T1  -- O4  -- T2  = 142.721 deg ; T1  -- T2   3.0678 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2315 A


        T-O-T SUMMARY
          Range  = 135.1709° <--> 180.0000 deg
          Mean   = 153.1557 deg
          StdDev = 19.1158 deg

        T--T SUMMARY
          Range  = 2.9988 A <--> 3.2315 A
          Mean   = 3.1067 A
          StdDev = 0.1027 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

<TD10> = 1025.000
Average ring size = 6.0000