Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_140758_1WKvJZ.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 26.37 T-atoms per nm^3
Material density = 2.631 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6327 Angstrom
T1  -- O3  = 1.6296 Angstrom
T1  -- O4  = 1.6419 Angstrom
T1  -- O2  = 1.6338 Angstrom
      mean = 1.6345 Angstrom
        t1 = 0.019777  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008532  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6201 Angstrom
T2  -- O3  = 1.6261 Angstrom
T2  -- O4  = 1.5852 Angstrom
T2  -- O5  = 1.6462 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.035838  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033492  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5852 A <--> 1.6462 A
          Mean   = 1.6269 A
          StdDev = 0.0177 A

       t1 Range  = 0.0198 <-- 0.0278 --> 0.0358
       t2 Range  = 0.0085 <-- 0.0210 --> 0.0335

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 111.249 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.416 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 111.394 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 111.476 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 106.053 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 108.227 deg; O4  -- O2  = 3 A
       106.053 deg <-- 109.469 deg --> 111.476 deg

O2  -- T2  -- O3  = 110.303 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 104.598 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 115.501 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 107.227 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 114.591 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 103.527 deg; O4  -- O5  = 3 A
       103.527 deg <-- 109.291 deg --> 115.501 deg

        O-T-O SUMMARY
          Range  = 103.5266 deg <--> 115.5009 deg
          Mean   = 109.3799 deg
          StdDev = 3.5836 deg

        O--O SUMMARY
          Range  = 2.5361 A <--> 2.7624 A
          Mean   = 2.6543 A
          StdDev = 0.0722 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  = 103.734 deg; T2  -- T2  = 4.6467 A
T2  - O1  - T1  - O4  - T1  = 113.972 deg; T2  -- T1  = 5.1202 A
T2  - O1  - T1  - O2  - T2  = 113.367 deg; T2  -- T2  = 5.1141 A
T2  - O3  - T1  - O4  - T1  = 112.138 deg; T2  -- T1  = 4.7561 A
T2  - O3  - T1  - O2  - T2  = 107.915 deg; T2  -- T2  = 4.6467 A
T1  - O4  - T1  - O2  - T2  = 105.715 deg; T1  -- T2  = 4.7426 A

T1  - O2  - T2  - O3  - T2  = 129.749 deg; T1  -- T2  = 5.8217 A
T1  - O2  - T2  - O4  - T1  = 113.367 deg; T1  -- T1  = 5.1141 A
T1  - O2  - T2  - O5  - T1  = 103.734 deg; T1  -- T1  = 4.6467 A
T2  - O3  - T2  - O4  - T1  = 114.190 deg; T2  -- T1  = 5.2702 A
T2  - O3  - T2  - O5  - T1  =  76.091 deg; T2  -- T1  = 3.7550 A
T1  - O4  - T2  - O5  - T1  = 107.915 deg; T1  -- T1  = 4.6467 A

        T-T-T SUMMARY
          Range  = 76.0906 deg <--> 129.7491 deg
          Mean   = 108.4905 deg
          StdDev = 11.8897 deg

        T--T SUMMARY
          Range  = 3.7550 A <--> 5.8217 A
          Mean   = 4.8567 A
          StdDev = 0.4784 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.692 deg ; T1  -- T1   2.9678 A

T1  -- O2  -- T2  = 132.800 deg ; T1  -- T2   2.9817 A

T1  -- O3  -- T2  = 149.014 deg ; T1  -- T2   3.1374 A

T1  -- O4  -- T2  = 117.766 deg ; T1  -- T2   2.7629 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2924 A


        T-O-T SUMMARY
          Range  = 117.7656° <--> 180.0000 deg
          Mean   = 142.0543 deg
          StdDev = 21.6878 deg

        T--T SUMMARY
          Range  = 2.7629 A <--> 3.2924 A
          Mean   = 3.0284 A
          StdDev = 0.1800 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7629 Angstrom
T2  -- T1  = 2.7629 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

<TD10> = 1025.000
Average ring size = 6.0000