Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_15_2_128381_vzxTwo.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.45 T-atoms per nm^3
Material density = 1.941 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6164 Angstrom
T1  -- O2  = 1.6162 Angstrom
T1  -- O4  = 1.6092 Angstrom
T1  -- O3  = 1.6222 Angstrom
      mean = 1.6160 Angstrom
        t1 = 0.004645  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003412  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6224 Angstrom
T2  -- O5  = 1.6165 Angstrom
T2  -- O6  = 1.6163 Angstrom
T2  -- O4  = 1.6093 Angstrom
      mean = 1.6161 Angstrom
        t1 = 0.004644  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002275  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6092 A <--> 1.6224 A
          Mean   = 1.6161 A
          StdDev = 0.0047 A

       t1 Range  = 0.0046 <-- 0.0046 --> 0.0046
       t2 Range  = 0.0023 <-- 0.0028 --> 0.0034

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.767 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.042 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.554 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.377 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.594 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.491 deg; O4  -- O3  = 3 A
       109.042 deg <-- 109.471 deg --> 109.767 deg

O3  -- T2  -- O5  = 109.528 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.543 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.502 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.779 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.061 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.412 deg; O6  -- O4  = 3 A
       109.061 deg <-- 109.471 deg --> 109.779 deg

        O-T-O SUMMARY
          Range  = 109.0420 deg <--> 109.7793 deg
          Mean   = 109.4435 deg
          StdDev = 0.2099 deg

        O--O SUMMARY
          Range  = 2.6267 A <--> 2.6461 A
          Mean   = 2.6385 A
          StdDev = 0.0073 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 119.107 deg; T1  -- T2  = 5.3625 A
T1  - O1  - T1  - O4  - T2  = 117.439 deg; T1  -- T2  = 5.4749 A
T1  - O1  - T1  - O3  - T1  = 103.033 deg; T1  -- T1  = 5.0263 A
T2  - O2  - T1  - O4  - T2  =  89.993 deg; T2  -- T2  = 4.4200 A
T2  - O2  - T1  - O3  - T1  = 118.682 deg; T2  -- T1  = 5.3888 A
T2  - O4  - T1  - O3  - T1  = 108.664 deg; T2  -- T1  = 5.2399 A

T2  - O3  - T2  - O5  - T2  = 103.042 deg; T2  -- T2  = 5.0270 A
T2  - O3  - T2  - O6  - T1  = 119.077 deg; T2  -- T1  = 5.3619 A
T2  - O3  - T2  - O4  - T1  = 117.454 deg; T2  -- T1  = 5.4757 A
T2  - O5  - T2  - O6  - T1  = 118.642 deg; T2  -- T1  = 5.3878 A
T2  - O5  - T2  - O4  - T1  = 108.705 deg; T2  -- T1  = 5.2415 A
T1  - O6  - T2  - O4  - T1  =  90.007 deg; T1  -- T1  = 4.4206 A

        T-T-T SUMMARY
          Range  = 89.9933 deg <--> 119.1067 deg
          Mean   = 108.6337 deg
          StdDev = 10.6237 deg

        T--T SUMMARY
          Range  = 4.4200 A <--> 5.4757 A
          Mean   = 5.1320 A
          StdDev = 0.3680 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 161.040 deg ; T1  -- T1   3.1886 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2323 A

T1  -- O3  -- T2  = 138.184 deg ; T1  -- T2   3.0309 A

T1  -- O4  -- T2  = 177.178 deg ; T1  -- T2   3.2175 A

T2  -- O5  -- T2  = 161.042 deg ; T2  -- T2   3.1889 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2325 A


        T-O-T SUMMARY
          Range  = 138.1837° <--> 180.0000 deg
          Mean   = 166.2405 deg
          StdDev = 15.0998 deg

        T--T SUMMARY
          Range  = 3.0309 A <--> 3.2325 A
          Mean   = 3.1818 A
          StdDev = 0.0706 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000