Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_159_2_1921_L1wK55.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 21.24 T-atoms per nm^3
Material density = 2.119 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6213 Angstrom
T1  -- O2  = 1.6214 Angstrom
T1  -- O3  = 1.6298 Angstrom
T1  -- O1  = 1.6219 Angstrom
      mean = 1.6236 Angstrom
        t1 = 0.013585  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012567  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6204 Angstrom
T2  -- O3  = 1.6298 Angstrom
T2  -- O4  = 1.6303 Angstrom
T2  -- O4  = 1.6223 Angstrom
      mean = 1.6257 Angstrom
        t1 = 0.013939  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006812  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6204 A <--> 1.6303 A
          Mean   = 1.6246 A
          StdDev = 0.0042 A

       t1 Range  = 0.0136 <-- 0.0138 --> 0.0139
       t2 Range  = 0.0068 <-- 0.0097 --> 0.0126

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.188 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.592 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.137 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 110.066 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 108.687 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 112.153 deg; O3  -- O1  = 3 A
       106.592 deg <-- 109.470 deg --> 112.153 deg

O2  -- T2  -- O3  = 109.588 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.824 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 110.525 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 112.027 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 107.106 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 108.764 deg; O4  -- O4  = 3 A
       107.106 deg <-- 109.472 deg --> 112.027 deg

        O-T-O SUMMARY
          Range  = 106.5922 deg <--> 112.1528 deg
          Mean   = 109.4714 deg
          StdDev = 1.6249 deg

        O--O SUMMARY
          Range  = 2.6065 A <--> 2.7031 A
          Mean   = 2.6528 A
          StdDev = 0.0276 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 105.085 deg; T1  -- T2  = 4.7507 A
T1  - O1  - T1  - O3  - T2  =  76.975 deg; T1  -- T2  = 3.6733 A
T1  - O1  - T1  - O1  - T1  = 109.368 deg; T1  -- T1  = 4.8249 A
T2  - O2  - T1  - O3  - T2  = 113.121 deg; T2  -- T2  = 4.9851 A
T2  - O2  - T1  - O1  - T1  = 134.431 deg; T2  -- T1  = 5.5175 A
T2  - O3  - T1  - O1  - T1  = 103.102 deg; T2  -- T1  = 4.6224 A

T1  - O2  - T2  - O3  - T1  = 112.540 deg; T1  -- T1  = 4.9683 A
T1  - O2  - T2  - O4  - T2  = 105.408 deg; T1  -- T2  = 4.7640 A
T1  - O2  - T2  - O4  - T2  = 134.823 deg; T1  -- T2  = 5.5290 A
T1  - O3  - T2  - O4  - T2  =  76.915 deg; T1  -- T2  = 3.6733 A
T1  - O3  - T2  - O4  - T2  = 103.008 deg; T1  -- T2  = 4.6224 A
T2  - O4  - T2  - O4  - T2  = 109.158 deg; T2  -- T2  = 4.8249 A

        T-T-T SUMMARY
          Range  = 76.9155 deg <--> 134.8228 deg
          Mean   = 106.9945 deg
          StdDev = 17.0721 deg

        T--T SUMMARY
          Range  = 3.6733 A <--> 5.5290 A
          Mean   = 4.7296 A
          StdDev = 0.5559 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.460 deg ; T1  -- T1   2.9565 A

T1  -- O2  -- T2  = 138.135 deg ; T1  -- T2   3.0279 A

T1  -- O3  -- T2  = 129.303 deg ; T1  -- T2   2.9458 A

T2  -- O4  -- T2  = 131.059 deg ; T2  -- T2   2.9604 A


        T-O-T SUMMARY
          Range  = 129.3035° <--> 138.1351 deg
          Mean   = 132.4892 deg
          StdDev = 3.4313 deg

        T--T SUMMARY
          Range  = 2.9458 A <--> 3.0279 A
          Mean   = 2.9726 A
          StdDev = 0.0331 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 20 34 54 78 104 134 168 210 256 302 352 406 470 538
TD10 = 817
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 20 34 54 78 104 134 168 210 256 302 352 406 470 538
TD10 = 817
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

<TD10> = 817.000
Average ring size = 5.1429