Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155_2_3627_KGTQ_e.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 20.27 T-atoms per nm^3
Material density = 2.022 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5205 Angstrom
T1  -- O2  = 1.7204 Angstrom
T1  -- O2  = 1.9167 Angstrom
T1  -- O3  = 1.6441 Angstrom
T1  -- O1  = 1.7361 Angstrom
      mean = 1.7076 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6317 Angstrom
T2  -- O4  = 1.6241 Angstrom
T2  -- O4  = 1.6201 Angstrom
T2  -- O5  = 1.6252 Angstrom
      mean = 1.6253 Angstrom
        t1 = 0.016583  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013044  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5205 A <--> 1.9167 A
          Mean   = 1.6710 A
          StdDev = 0.1051 A

       t1 Range  = 0.0166 <-- 0.0083 --> 0.0166
       t2 Range  = 0.0130 <-- 0.0065 --> 0.0130

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  74.870 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  = 128.257 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.183 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  =  92.617 deg; O1  -- O1  = 2 A
O2  -- T1  -- O2  =  82.884 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  = 117.766 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 127.356 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 122.511 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  =  65.294 deg; O2  -- O1  = 2 A
O3  -- T1  -- O1  = 114.668 deg; O3  -- O1  = 3 A
       65.294 deg <-- 103.541 deg --> 128.257 deg

O3  -- T2  -- O4  = 107.796 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 111.942 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 110.695 deg; O3  -- O5  = 3 A
O4  -- T2  -- O4  = 107.887 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 111.846 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 106.687 deg; O4  -- O5  = 3 A
       106.687 deg <-- 109.475 deg --> 111.942 deg

        O-T-O SUMMARY
          Range  = 65.2938 deg <--> 128.2573 deg
          Mean   = 106.5043 deg
          StdDev = 17.2862 deg

        O--O SUMMARY
          Range  = 1.9764 A <--> 3.1248 A
          Mean   = 2.6495 A
          StdDev = 0.3367 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  99.208 deg ; T1  -- T1   2.4841 A

T1  -- O2  -- T1  =  85.979 deg ; T1  -- T1   2.4841 A
T1  -- O2  -- T1  = 142.645 deg ; T1  -- T1   3.2595 A
T1  -- O2  -- T1  =  78.483 deg ; T1  -- T1   2.3058 A
T1  -- O2  -- T1  =  78.483 deg ; T1  -- T1   2.3058 A
T1  -- O2  -- T1  = 130.178 deg ; T1  -- T1   3.4767 A
T1  -- O2  -- T1  =  85.979 deg ; T1  -- T1   2.4841 A

T1  -- O3  -- T2  = 123.995 deg ; T1  -- T2   2.8923 A

T2  -- O4  -- T2  = 130.911 deg ; T2  -- T2   2.9510 A

T2  -- O5  -- T2  = 126.561 deg ; T2  -- T2   2.9032 A


        T-O-T SUMMARY
          Range  = 78.4833° <--> 142.6452 deg
          Mean   = 108.2422 deg
          StdDev = 23.7440 deg

        T--T SUMMARY
          Range  = 2.3058 A <--> 3.4767 A
          Mean   = 2.7547 A
          StdDev = 0.3856 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.9764 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T2  = 2.8923 Angstrom
  T1  -- T1  = 3.4767 Angstrom
  T1  -- T1  = 2.4841 Angstrom
  T1  -- T1  = 3.2595 Angstrom
  T1  -- T1  = 2.4841 Angstrom
  T1  -- T1  = 2.3058 Angstrom