Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155_2_121481_lI7pRY.cif"

There are 18 T-atoms per unit cell
There are 36 O-atoms per unit cell

Framework density = 28.97 T-atoms per nm^3
Material density = 2.890 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6341 Angstrom
T1  -- O2  = 1.6353 Angstrom
T1  -- O1  = 1.6341 Angstrom
T1  -- O2  = 1.6353 Angstrom
      mean = 1.6347 Angstrom
        t1 = 0.084040  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060835  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6435 Angstrom
T2  -- O1  = 1.6435 Angstrom
T2  -- O2  = 1.6512 Angstrom
T2  -- O2  = 1.6512 Angstrom
      mean = 1.6474 Angstrom
        t1 = 0.077835  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061918  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6341 A <--> 1.6512 A
          Mean   = 1.6410 A
          StdDev = 0.0069 A

       t1 Range  = 0.0778 <-- 0.0809 --> 0.0840
       t2 Range  = 0.0608 <-- 0.0614 --> 0.0619

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  97.344 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  = 101.312 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 129.883 deg; O1  -- O2  = 3 A
O2  -- T1  -- O1  = 129.883 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 105.322 deg; O2  -- O2  = 3 A
O1  -- T1  -- O2  =  97.344 deg; O1  -- O2  = 2 A
       97.344 deg <-- 110.181 deg --> 129.883 deg

O1  -- T2  -- O1  = 102.368 deg; O1  -- O1  = 3 A
O1  -- T2  -- O2  =  99.230 deg; O1  -- O2  = 3 A
O1  -- T2  -- O2  = 127.794 deg; O1  -- O2  = 3 A
O1  -- T2  -- O2  = 127.794 deg; O1  -- O2  = 3 A
O1  -- T2  -- O2  =  99.234 deg; O1  -- O2  = 3 A
O2  -- T2  -- O2  = 103.833 deg; O2  -- O2  = 3 A
       99.230 deg <-- 110.042 deg --> 127.794 deg

        O-T-O SUMMARY
          Range  = 97.3440 deg <--> 129.8832 deg
          Mean   = 110.1118 deg
          StdDev = 13.4776 deg

        O--O SUMMARY
          Range  = 2.4552 A <--> 2.9617 A
          Mean   = 2.6716 A
          StdDev = 0.2092 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  91.298 deg; T2  -- T2  = 4.4654 A
T2  - O1  - T1  - O1  - T2  = 142.866 deg; T2  -- T2  = 5.9196 A
T2  - O1  - T1  - O2  - T2  = 119.879 deg; T2  -- T2  = 5.4102 A
T2  - O2  - T1  - O1  - T2  =  70.155 deg; T2  -- T2  = 3.5851 A
T2  - O2  - T1  - O2  - T2  = 142.865 deg; T2  -- T2  = 5.9196 A
T2  - O1  - T1  - O2  - T2  =  91.298 deg; T2  -- T2  = 4.4653 A

T1  - O1  - T2  - O1  - T1  =  91.213 deg; T1  -- T1  = 4.4622 A
T1  - O1  - T2  - O2  - T1  = 120.048 deg; T1  -- T1  = 5.4039 A
T1  - O1  - T2  - O2  - T1  = 142.865 deg; T1  -- T1  = 5.9196 A
T1  - O1  - T2  - O2  - T1  = 142.866 deg; T1  -- T1  = 5.9196 A
T1  - O1  - T2  - O2  - T1  =  70.028 deg; T1  -- T1  = 3.5866 A
T1  - O2  - T2  - O2  - T1  =  91.216 deg; T1  -- T1  = 4.4622 A

        T-T-T SUMMARY
          Range  = 70.0282 deg <--> 142.8660 deg
          Mean   = 109.7164 deg
          StdDev = 27.6151 deg

        T--T SUMMARY
          Range  = 3.5851 A <--> 5.9196 A
          Mean   = 4.9600 A
          StdDev = 0.8605 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 144.947 deg ; T1  -- T2   3.1255 A

T1  -- O2  -- T2  = 143.276 deg ; T1  -- T2   3.1192 A


        T-O-T SUMMARY
          Range  = 143.2757° <--> 144.9465 deg
          Mean   = 144.1111 deg
          StdDev = 0.8597 deg

        T--T SUMMARY
          Range  = 3.1192 A <--> 3.1255 A
          Mean   = 3.1224 A
          StdDev = 0.0032 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 9
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

T2 (Si): multiplicity = 9
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

<TD10> = 1169.000
Average ring size = 6.5455