Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155_1_86_2jPvlE.cif"

There are 9 T-atoms per unit cell
There are 18 O-atoms per unit cell

Framework density = 30.57 T-atoms per nm^3
Material density = 3.050 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6743 Angstrom
T1  -- O2  = 1.6742 Angstrom
T1  -- O1  = 1.6632 Angstrom
T1  -- O1  = 1.6631 Angstrom
      mean = 1.6687 Angstrom
        t1 = 0.114217  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.070219  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6631 A <--> 1.6743 A
          Mean   = 1.6687 A
          StdDev = 0.0056 A

       t1 Range  = 0.1142 <-- 0.1142 --> 0.1142
       t2 Range  = 0.0702 <-- 0.0702 --> 0.0702

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O2  = 106.774 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  = 104.045 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 131.166 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 131.167 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 104.046 deg; O2  -- O1  = 3 A
O1  -- T1  -- O1  =  81.895 deg; O1  -- O1  = 2 A
       81.895 deg <-- 109.849 deg --> 131.167 deg

        O-T-O SUMMARY
          Range  = 81.8951 deg <--> 131.1668 deg
          Mean   = 109.8489 deg
          StdDev = 17.3226 deg

        O--O SUMMARY
          Range  = 2.1800 A <--> 3.0389 A
          Mean   = 2.7012 A
          StdDev = 0.2943 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O2  - T1  =  78.916 deg; T1  -- T1  = 3.8042 A
T1  - O2  - T1  - O1  - T1  = 167.999 deg; T1  -- T1  = 5.8986 A
T1  - O2  - T1  - O1  - T1  =  92.481 deg; T1  -- T1  = 4.7662 A
T1  - O2  - T1  - O1  - T1  = 110.758 deg; T1  -- T1  = 4.3304 A
T1  - O2  - T1  - O1  - T1  = 167.999 deg; T1  -- T1  = 5.8986 A
T1  - O1  - T1  - O1  - T1  =  78.916 deg; T1  -- T1  = 3.8042 A

        T-T-T SUMMARY
          Range  = 78.9160 deg <--> 167.9988 deg
          Mean   = 116.1781 deg
          StdDev = 38.5217 deg

        T--T SUMMARY
          Range  = 3.8042 A <--> 5.8986 A
          Mean   = 4.7504 A
          StdDev = 0.8842 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 104.558 deg ; T1  -- T1   2.6311 A

T1  -- O2  -- T1  = 160.395 deg ; T1  -- T1   3.2996 A


        T-O-T SUMMARY
          Range  = 104.5576° <--> 160.3948 deg
          Mean   = 132.4762 deg
          StdDev = 28.7280 deg

        T--T SUMMARY
          Range  = 2.6311 A <--> 3.2996 A
          Mean   = 2.9653 A
          StdDev = 0.3439 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.1800 A
O1  -- O1  = 2.1800 A
T1  -- T1  = 2.6311 Angstrom
T1  -- T1  = 2.6311 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 9
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

<TD10> = 1169.000
Average ring size = 6.5455