Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155_1_32_Txfaq5.cif"

There are 18 T-atoms per unit cell
There are 36 O-atoms per unit cell

Framework density = 32.08 T-atoms per nm^3
Material density = 3.201 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6558 Angstrom
T1  -- O2  = 1.6790 Angstrom
T1  -- O3  = 1.6790 Angstrom
T1  -- O4  = 1.6558 Angstrom
      mean = 1.6674 Angstrom
        t1 = 0.104949  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.063621  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6558 A <--> 1.6790 A
          Mean   = 1.6674 A
          StdDev = 0.0117 A

       t1 Range  = 0.1049 <-- 0.1049 --> 0.1049
       t2 Range  = 0.0636 <-- 0.0636 --> 0.0636

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 129.369 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.944 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  84.800 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 105.626 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 104.990 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 129.384 deg; O3  -- O4  = 3 A
       84.800 deg <-- 109.852 deg --> 129.384 deg

        O-T-O SUMMARY
          Range  = 84.8005 deg <--> 129.3840 deg
          Mean   = 109.8521 deg
          StdDev = 15.7217 deg

        O--O SUMMARY
          Range  = 2.2330 A <--> 3.0148 A
          Mean   = 2.7046 A
          StdDev = 0.2679 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 165.762 deg; T1  -- T1  = 5.8209 A
T1  - O1  - T1  - O3  - T1  =  77.711 deg; T1  -- T1  = 3.7272 A
T1  - O1  - T1  - O4  - T1  = 113.984 deg; T1  -- T1  = 4.2789 A
T1  - O2  - T1  - O3  - T1  =  92.128 deg; T1  -- T1  = 4.7734 A
T1  - O2  - T1  - O4  - T1  =  77.669 deg; T1  -- T1  = 3.7261 A
T1  - O3  - T1  - O4  - T1  = 165.707 deg; T1  -- T1  = 5.8209 A

        T-T-T SUMMARY
          Range  = 77.6692 deg <--> 165.7618 deg
          Mean   = 115.4935 deg
          StdDev = 37.8908 deg

        T--T SUMMARY
          Range  = 3.7261 A <--> 5.8209 A
          Mean   = 4.6912 A
          StdDev = 0.8829 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 100.796 deg ; T1  -- T1   2.5515 A

T1  -- O2  -- T1  = 161.475 deg ; T1  -- T1   3.3142 A

T1  -- O3  -- T1  = 161.513 deg ; T1  -- T1   3.3144 A

T1  -- O4  -- T1  = 100.762 deg ; T1  -- T1   2.5510 A


        T-O-T SUMMARY
          Range  = 100.7624° <--> 161.5130 deg
          Mean   = 131.1366 deg
          StdDev = 30.5703 deg

        T--T SUMMARY
          Range  = 2.5510 A <--> 3.3144 A
          Mean   = 2.9328 A
          StdDev = 0.3842 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2330 A
O1  -- O4  = 2.2330 A
T1  -- T1  = 2.5510 Angstrom
T1  -- T1  = 2.5515 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

<TD10> = 1169.000
Average ring size = 6.5455