Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_920_ffex0T.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 14.10 T-atoms per nm^3
Material density = 1.407 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6344 Angstrom
T1  -- O4  = 1.8053 Angstrom
T1  -- O4  = 1.8053 Angstrom
T1  -- O3  = 1.8051 Angstrom
T1  -- O1  = 1.6347 Angstrom
T1  -- O3  = 1.8051 Angstrom
      mean = 1.7483 Angstrom

        T-O SUMMARY
          Range  = 1.6344 A <--> 1.8053 A
          Mean   = 1.7483 A
          StdDev = 0.0816 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O4  =  79.694 deg; O2  -- O4  = 2 A
O2  -- T1  -- O4  =  79.692 deg; O2  -- O4  = 2 A
O2  -- T1  -- O3  = 136.204 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  =  89.687 deg; O2  -- O1  = 2 A
O2  -- T1  -- O3  = 136.209 deg; O2  -- O3  = 3 A
O4  -- T1  -- O4  =  83.770 deg; O4  -- O4  = 2 A
O4  -- T1  -- O3  = 134.972 deg; O4  -- O3  = 3 A
O4  -- T1  -- O1  = 136.196 deg; O4  -- O1  = 3 A
O4  -- T1  -- O3  =  79.364 deg; O4  -- O3  = 2 A
O4  -- T1  -- O3  =  79.360 deg; O4  -- O3  = 2 A
O4  -- T1  -- O1  = 136.190 deg; O4  -- O1  = 3 A
O4  -- T1  -- O3  = 134.972 deg; O4  -- O3  = 3 A
O3  -- T1  -- O1  =  79.710 deg; O3  -- O1  = 2 A
O3  -- T1  -- O3  =  83.756 deg; O3  -- O3  = 2 A
O1  -- T1  -- O3  =  79.712 deg; O1  -- O3  = 2 A
       79.360 deg <-- 103.299 deg --> 136.209 deg

        O-T-O SUMMARY
          Range  = 79.3604 deg <--> 136.2094 deg
          Mean   = 103.2993 deg
          StdDev = 26.9571 deg

        O--O SUMMARY
          Range  = 2.2078 A <--> 3.3352 A
          Mean   = 2.6672 A
          StdDev = 0.4789 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  89.671 deg ; T1  -- T1   2.3052 A

T1  -- O2  -- T1  =  89.703 deg ; T1  -- T1   2.3054 A

T1  -- O3  -- T1  =  83.433 deg ; T1  -- T1   2.4024 A
T1  -- O3  -- T1  =  79.363 deg ; T1  -- T1   2.3052 A
T1  -- O3  -- T1  = 134.513 deg ; T1  -- T1   3.3294 A
T1  -- O3  -- T1  = 134.509 deg ; T1  -- T1   3.3295 A
T1  -- O3  -- T1  =  79.363 deg ; T1  -- T1   2.3052 A
T1  -- O3  -- T1  =  83.433 deg ; T1  -- T1   2.4024 A

T1  -- O4  -- T1  =  83.421 deg ; T1  -- T1   2.4024 A
T1  -- O4  -- T1  =  79.362 deg ; T1  -- T1   2.3054 A
T1  -- O4  -- T1  = 134.494 deg ; T1  -- T1   3.3296 A
T1  -- O4  -- T1  = 134.490 deg ; T1  -- T1   3.3297 A
T1  -- O4  -- T1  =  79.362 deg ; T1  -- T1   2.3054 A
T1  -- O4  -- T1  =  83.421 deg ; T1  -- T1   2.4024 A


        T-O-T SUMMARY
          Range  = 79.3616° <--> 134.5132 deg
          Mean   = 97.7526 deg
          StdDev = 23.6018 deg

        T--T SUMMARY
          Range  = 2.3052 A <--> 3.3297 A
          Mean   = 2.6257 A
          StdDev = 0.4497 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.2083 A
O1  -- O3  = 2.2083 A
O2  -- O4  = 2.2078 A
O2  -- O4  = 2.2078 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 8 neighboring T-atoms within 3.50 A, but only 6 bridging O-atoms
  T1  -- T1  = 2.4024 Angstrom
  T1  -- T1  = 2.4024 Angstrom
  T1  -- T1  = 2.3054 Angstrom
  T1  -- T1  = 3.3297 Angstrom
  T1  -- T1  = 3.3296 Angstrom
  T1  -- T1  = 2.3052 Angstrom
  T1  -- T1  = 3.3295 Angstrom
  T1  -- T1  = 3.3294 Angstrom