Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_185_hB16YL.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.22 T-atoms per nm^3
Material density = 3.314 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8541 Angstrom
T1  -- O2  = 1.9228 Angstrom
T1  -- O1  = 1.7441 Angstrom
T1  -- O1  = 1.7811 Angstrom
T1  -- O2  = 1.6339 Angstrom
T1  -- O3  = 1.8575 Angstrom
T1  -- O3  = 1.9454 Angstrom
      mean = 1.8199 Angstrom

        T-O SUMMARY
          Range  = 1.6339 A <--> 1.9454 A
          Mean   = 1.8199 A
          StdDev = 0.1018 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  85.110 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 125.823 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  =  85.820 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  42.779 deg; O1  -- O2  = 1 A
O1  -- T1  -- O3  = 129.958 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  76.772 deg; O1  -- O3  = 2 A
O2  -- T1  -- O1  =  40.781 deg; O2  -- O1  = 1 A
O2  -- T1  -- O1  =  98.925 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  =  85.302 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  = 144.480 deg; O2  -- O3  = 4 A
O2  -- T1  -- O3  = 126.235 deg; O2  -- O3  = 3 A
O1  -- T1  -- O1  =  97.976 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 112.933 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.789 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 131.096 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  =  44.072 deg; O1  -- O2  = 1 A
O1  -- T1  -- O3  =  80.859 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  = 128.932 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 115.429 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 110.942 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  =  75.123 deg; O3  -- O3  = 2 A
       40.781 deg <-- 97.292 deg --> 144.480 deg

        O-T-O SUMMARY
          Range  = 40.7809 deg <--> 144.4800 deg
          Mean   = 95.2434 deg
          StdDev = 30.2470 deg

        O--O SUMMARY
          Range  = 1.2885 A <--> 3.6002 A
          Mean   = 2.6046 A
          StdDev = 0.6942 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  51.311 deg ; T1  -- T1   1.5753 A
T1  -- O1  -- T1  = 120.414 deg ; T1  -- T1   3.1231 A
T1  -- O1  -- T1  =  73.590 deg ; T1  -- T1   2.1117 A

T1  -- O2  -- T1  =  72.327 deg ; T1  -- T1   2.1117 A
T1  -- O2  -- T1  = 122.624 deg ; T1  -- T1   3.1231 A
T1  -- O2  -- T1  = 164.550 deg ; T1  -- T1   3.8106 A
T1  -- O2  -- T1  =  57.642 deg ; T1  -- T1   1.5753 A
T1  -- O2  -- T1  = 122.624 deg ; T1  -- T1   3.1231 A
T1  -- O2  -- T1  =  72.327 deg ; T1  -- T1   2.1117 A

T1  -- O3  -- T1  =  48.874 deg ; T1  -- T1   1.5753 A
T1  -- O3  -- T1  = 154.822 deg ; T1  -- T1   3.7973 A
T1  -- O3  -- T1  = 125.979 deg ; T1  -- T1   3.3884 A
T1  -- O3  -- T1  = 125.979 deg ; T1  -- T1   3.3884 A
T1  -- O3  -- T1  = 161.460 deg ; T1  -- T1   3.6665 A
T1  -- O3  -- T1  =  48.874 deg ; T1  -- T1   1.5753 A


        T-O-T SUMMARY
          Range  = 48.8744° <--> 164.5499 deg
          Mean   = 101.5600 deg
          StdDev = 41.3193 deg

        T--T SUMMARY
          Range  = 1.5753 A <--> 3.8106 A
          Mean   = 2.6705 A
          StdDev = 0.8589 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.2885 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 6 neighboring T-atoms within 3.50 A, but 7 bridging O-atoms
  T1  -- T1  = 2.1117 Angstrom
  T1  -- T1  = 3.1231 Angstrom
  T1  -- T1  = 3.3884 Angstrom
  T1  -- T1  = 3.1231 Angstrom
  T1  -- T1  = 1.5753 Angstrom
  T1  -- T1  = 3.3884 Angstrom