Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_1660_013jx8.cif"

There are 3 T-atoms per unit cell
There are 6 O-atoms per unit cell

Framework density = 10.75 T-atoms per nm^3
Material density = 1.072 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8414 Angstrom
T1  -- O1  = 1.8414 Angstrom
T1  -- O2  = 1.6408 Angstrom
T1  -- O1  = 1.8414 Angstrom
T1  -- O1  = 1.8414 Angstrom
T1  -- O2  = 1.6408 Angstrom
      mean = 1.7745 Angstrom

        T-O SUMMARY
          Range  = 1.6408 A <--> 1.8414 A
          Mean   = 1.7745 A
          StdDev = 0.0973 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  84.334 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  77.127 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  =  80.710 deg; O1  -- O1  = 2 A
O1  -- T1  -- O1  = 137.717 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 135.916 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  77.127 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  = 137.717 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  =  80.710 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 135.916 deg; O1  -- O2  = 3 A
O2  -- T1  -- O1  = 135.916 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 135.916 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  =  93.221 deg; O2  -- O2  = 2 A
O1  -- T1  -- O1  =  84.334 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  77.127 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  =  77.127 deg; O1  -- O2  = 2 A
       77.127 deg <-- 103.394 deg --> 137.717 deg

        O-T-O SUMMARY
          Range  = 77.1271 deg <--> 137.7171 deg
          Mean   = 103.3943 deg
          StdDev = 27.6412 deg

        O--O SUMMARY
          Range  = 2.1764 A <--> 3.4350 A
          Mean   = 2.7059 A
          StdDev = 0.5020 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  80.781 deg ; T1  -- T1   2.3865 A
T1  -- O1  -- T1  =  80.710 deg ; T1  -- T1   2.3847 A
T1  -- O1  -- T1  = 132.716 deg ; T1  -- T1   3.3737 A
T1  -- O1  -- T1  = 132.716 deg ; T1  -- T1   3.3737 A
T1  -- O1  -- T1  =  80.710 deg ; T1  -- T1   2.3847 A
T1  -- O1  -- T1  =  80.781 deg ; T1  -- T1   2.3865 A

T1  -- O2  -- T1  =  93.221 deg ; T1  -- T1   2.3847 A


        T-O-T SUMMARY
          Range  = 80.7101° <--> 132.7162 deg
          Mean   = 97.3766 deg
          StdDev = 23.3068 deg

        T--T SUMMARY
          Range  = 2.3847 A <--> 3.3737 A
          Mean   = 2.6678 A
          StdDev = 0.4575 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.1764 A
O1  -- O2  = 2.1764 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 8 neighboring T-atoms within 3.50 A, but only 6 bridging O-atoms
  T1  -- T1  = 2.3865 Angstrom
  T1  -- T1  = 2.3865 Angstrom
  T1  -- T1  = 2.3847 Angstrom
  T1  -- T1  = 3.3737 Angstrom
  T1  -- T1  = 3.3737 Angstrom
  T1  -- T1  = 2.3847 Angstrom
  T1  -- T1  = 3.3737 Angstrom
  T1  -- T1  = 3.3737 Angstrom