Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_1624_EFyoFz.cif"

There are 3 T-atoms per unit cell
There are 6 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.325 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6980 Angstrom
T1  -- O2  = 1.6477 Angstrom
T1  -- O1  = 1.6980 Angstrom
T1  -- O2  = 1.6477 Angstrom
      mean = 1.6728 Angstrom
        t1 = 0.101622  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076808  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6477 A <--> 1.6980 A
          Mean   = 1.6728 A
          StdDev = 0.0263 A

       t1 Range  = 0.1016 <-- 0.1016 --> 0.1016
       t2 Range  = 0.0768 <-- 0.0768 --> 0.0768

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 100.089 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 118.262 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 124.397 deg; O1  -- O2  = 3 A
O2  -- T1  -- O1  = 124.397 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  =  87.689 deg; O2  -- O2  = 2 A
O1  -- T1  -- O2  = 100.089 deg; O1  -- O2  = 3 A
       87.689 deg <-- 109.153 deg --> 124.397 deg

        O-T-O SUMMARY
          Range  = 87.6885 deg <--> 124.3967 deg
          Mean   = 109.1535 deg
          StdDev = 14.3860 deg

        O--O SUMMARY
          Range  = 2.2827 A <--> 2.9595 A
          Mean   = 2.7077 A
          StdDev = 0.2628 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  74.601 deg; T1  -- T1  = 3.5883 A
T1  - O1  - T1  - O1  - T1  =  95.355 deg; T1  -- T1  = 4.8347 A
T1  - O1  - T1  - O2  - T1  = 166.205 deg; T1  -- T1  = 5.8105 A
T1  - O2  - T1  - O1  - T1  = 166.205 deg; T1  -- T1  = 5.8105 A
T1  - O2  - T1  - O2  - T1  = 116.798 deg; T1  -- T1  = 4.3995 A
T1  - O1  - T1  - O2  - T1  =  74.601 deg; T1  -- T1  = 3.5883 A

        T-T-T SUMMARY
          Range  = 74.6014 deg <--> 166.2049 deg
          Mean   = 115.6276 deg
          StdDev = 39.6190 deg

        T--T SUMMARY
          Range  = 3.5883 A <--> 5.8105 A
          Mean   = 4.6720 A
          StdDev = 0.9433 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 148.634 deg ; T1  -- T1   3.2695 A

T1  -- O2  -- T1  = 103.210 deg ; T1  -- T1   2.5827 A


        T-O-T SUMMARY
          Range  = 103.2102° <--> 148.6340 deg
          Mean   = 125.9221 deg
          StdDev = 24.8797 deg

        T--T SUMMARY
          Range  = 2.5827 A <--> 3.2695 A
          Mean   = 2.9261 A
          StdDev = 0.3762 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.0387 A
O1  -- O1  = 2.0387 A
O2  -- O2  = 2.2827 A
O2  -- O2  = 2.2827 A
T1  -- T1  = 2.5827 Angstrom
T1  -- T1  = 2.5827 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 3
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

<TD10> = 1169.000
Average ring size = 6.5455