Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_158_LFdf0p.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.325 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8360 Angstrom
T1  -- O1  = 2.0863 Angstrom
T1  -- O3  = 1.8731 Angstrom
T1  -- O1  = 1.8623 Angstrom
T1  -- O2  = 1.4339 Angstrom
      mean = 1.8183 Angstrom

        T-O SUMMARY
          Range  = 1.4339 A <--> 2.0863 A
          Mean   = 1.8183 A
          StdDev = 0.2157 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  99.639 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 118.010 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 110.214 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  54.918 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  73.971 deg; O1  -- O3  = 2 A
O1  -- T1  -- O1  =  89.932 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  47.942 deg; O1  -- O2  = 2 A
O3  -- T1  -- O1  = 130.890 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  =  83.897 deg; O3  -- O2  = 2 A
O1  -- T1  -- O2  = 118.916 deg; O1  -- O2  = 3 A
       47.942 deg <-- 92.833 deg --> 130.890 deg

        O-T-O SUMMARY
          Range  = 47.9424 deg <--> 130.8897 deg
          Mean   = 93.3033 deg
          StdDev = 27.3189 deg

        O--O SUMMARY
          Range  = 1.5495 A <--> 3.3975 A
          Mean   = 2.6166 A
          StdDev = 0.6327 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 125.043 deg ; T1  -- T1   3.2811 A
T1  -- O1  -- T1  =  75.849 deg ; T1  -- T1   2.4188 A
T1  -- O1  -- T1  =  60.830 deg ; T1  -- T1   2.0083 A

T1  -- O2  -- T1  = 115.008 deg ; T1  -- T1   2.4188 A

T1  -- O3  -- T1  = 174.269 deg ; T1  -- T1   3.7415 A


        T-O-T SUMMARY
          Range  = 60.8295° <--> 174.2690 deg
          Mean   = 110.1999 deg
          StdDev = 40.5965 deg

        T--T SUMMARY
          Range  = 2.0083 A <--> 3.7415 A
          Mean   = 2.7737 A
          StdDev = 0.6484 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.5495 A
O2  -- O3  = 2.2346 A
O2  -- O3  = 2.2346 A
O3  -- O3  = 2.2953 A
O3  -- O3  = 2.2953 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.4982 Angstrom
  T1  -- T1  = 3.4982 Angstrom
  T1  -- T1  = 2.0083 Angstrom
  T1  -- T1  = 2.4188 Angstrom
  T1  -- T1  = 3.2811 Angstrom
  T1  -- T1  = 3.4176 Angstrom
  T1  -- T1  = 3.2811 Angstrom