Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_1575_rNs3Eo.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 31.45 T-atoms per nm^3
Material density = 3.138 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6593 Angstrom
T1  -- O3  = 1.6480 Angstrom
T1  -- O2  = 1.6819 Angstrom
T1  -- O4  = 1.6548 Angstrom
      mean = 1.6610 Angstrom
        t1 = 0.115754  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.099335  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6480 A <--> 1.6819 A
          Mean   = 1.6610 A
          StdDev = 0.0130 A

       t1 Range  = 0.1158 <-- 0.1158 --> 0.1158
       t2 Range  = 0.0993 <-- 0.0993 --> 0.0993

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 112.021 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 125.189 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 108.658 deg; O1  -- O4  = 3 A
O3  -- T1  -- O2  =  79.491 deg; O3  -- O2  = 2 A
O3  -- T1  -- O4  = 132.520 deg; O3  -- O4  = 3 A
O2  -- T1  -- O4  =  96.418 deg; O2  -- O4  = 2 A
       79.491 deg <-- 109.050 deg --> 132.520 deg

        O-T-O SUMMARY
          Range  = 79.4908 deg <--> 132.5204 deg
          Mean   = 109.0497 deg
          StdDev = 18.0861 deg

        O--O SUMMARY
          Range  = 2.1292 A <--> 3.0233 A
          Mean   = 2.6735 A
          StdDev = 0.3098 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T1  =  88.002 deg; T1  -- T1  = 4.0261 A
T1  - O1  - T1  - O2  - T1  = 158.873 deg; T1  -- T1  = 5.8275 A
T1  - O1  - T1  - O4  - T1  =  91.998 deg; T1  -- T1  = 4.6614 A
T1  - O3  - T1  - O2  - T1  = 107.881 deg; T1  -- T1  = 4.2654 A
T1  - O3  - T1  - O4  - T1  = 180.000 deg; T1  -- T1  = 5.8275 A
T1  - O2  - T1  - O4  - T1  =  72.119 deg; T1  -- T1  = 3.5591 A

        T-T-T SUMMARY
          Range  = 72.1193 deg <--> 180.0000 deg
          Mean   = 116.4789 deg
          StdDev = 40.4769 deg

        T--T SUMMARY
          Range  = 3.5591 A <--> 5.8275 A
          Mean   = 4.6945 A
          StdDev = 0.8900 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 149.831 deg ; T1  -- T1   3.2043 A

T1  -- O2  -- T1  = 108.094 deg ; T1  -- T1   2.7230 A

T1  -- O3  -- T1  = 101.469 deg ; T1  -- T1   2.5519 A

T1  -- O4  -- T1  = 163.572 deg ; T1  -- T1   3.2756 A


        T-O-T SUMMARY
          Range  = 101.4689° <--> 163.5718 deg
          Mean   = 130.7416 deg
          StdDev = 27.0845 deg

        T--T SUMMARY
          Range  = 2.5519 A <--> 3.2756 A
          Mean   = 2.9387 A
          StdDev = 0.3149 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 2.1292 A
O2  -- O3  = 2.1292 A
T1  -- T1  = 2.5519 Angstrom
T1  -- T1  = 2.7230 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

<TD10> = 1169.000
Average ring size = 6.5455