Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_139_DjCjp0.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.325 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6881 Angstrom
T1  -- O1  = 1.0934 Angstrom
T1  -- O1  = 1.7217 Angstrom
T1  -- O2  = 1.7378 Angstrom
T1  -- O3  = 1.7111 Angstrom
      mean = 1.5904 Angstrom

        T-O SUMMARY
          Range  = 1.0934 A <--> 1.7378 A
          Mean   = 1.5904 A
          StdDev = 0.2533 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  16.444 deg; O1  -- O1  = 1 A
O1  -- T1  -- O1  =  24.025 deg; O1  -- O1  = 1 A
O1  -- T1  -- O2  = 131.471 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.976 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  =  13.878 deg; O1  -- O1  = 1 A
O1  -- T1  -- O2  = 115.630 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 122.349 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 108.291 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.609 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 112.349 deg; O2  -- O3  = 3 A
       13.878 deg <-- 87.102 deg --> 131.471 deg

        O-T-O SUMMARY
          Range  = 13.8775 deg <--> 131.4711 deg
          Mean   = 85.7732 deg
          StdDev = 46.9352 deg

        O--O SUMMARY
          Range  = 0.7104 A <--> 3.1233 A
          Mean   = 2.1143 A
          StdDev = 0.9831 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  90.095 deg ; T1  -- T1   2.4132 A
T1  -- O1  -- T1  = 118.800 deg ; T1  -- T1   2.4132 A
T1  -- O1  -- T1  = 116.227 deg ; T1  -- T1   2.4132 A

T1  -- O2  -- T1  = 169.114 deg ; T1  -- T1   3.4600 A

T1  -- O3  -- T1  = 136.089 deg ; T1  -- T1   3.1740 A


        T-O-T SUMMARY
          Range  = 90.0947° <--> 169.1137 deg
          Mean   = 126.0650 deg
          StdDev = 26.5113 deg

        T--T SUMMARY
          Range  = 2.4132 A <--> 3.4600 A
          Mean   = 2.7747 A
          StdDev = 0.4597 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 0.7104 A
O1  -- O1  = 0.7104 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 2.4132 Angstrom
  T1  -- T1  = 2.4132 Angstrom
  T1  -- T1  = 3.2941 Angstrom
  T1  -- T1  = 3.1740 Angstrom
  T1  -- T1  = 3.4600 Angstrom
  T1  -- T1  = 3.1813 Angstrom