Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_155-2_1_133_QaANLi.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8772 Angstrom
T1  -- O1  = 1.6885 Angstrom
T1  -- O2  = 1.8138 Angstrom
T1  -- O2  = 1.5849 Angstrom
T1  -- O3  = 1.6033 Angstrom
T1  -- O3  = 2.0001 Angstrom
      mean = 1.7613 Angstrom

        T-O SUMMARY
          Range  = 1.5849 A <--> 2.0001 A
          Mean   = 1.7613 A
          StdDev = 0.1519 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  86.538 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  39.199 deg; O1  -- O2  = 1 A
O1  -- T1  -- O2  = 114.992 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  88.572 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  = 139.010 deg; O1  -- O3  = 4 A
O1  -- T1  -- O2  = 113.079 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  44.365 deg; O1  -- O2  = 1 A
O1  -- T1  -- O3  = 113.759 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 133.568 deg; O1  -- O3  = 3 A
O2  -- T1  -- O2  = 114.644 deg; O2  -- O2  = 3 A
O2  -- T1  -- O3  = 102.568 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 104.295 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 141.911 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  =  95.555 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  =  82.381 deg; O3  -- O3  = 2 A
       39.199 deg <-- 100.962 deg --> 141.911 deg

        O-T-O SUMMARY
          Range  = 39.1993 deg <--> 141.9112 deg
          Mean   = 99.4800 deg
          StdDev = 31.1708 deg

        O--O SUMMARY
          Range  = 1.2396 A <--> 3.6322 A
          Mean   = 2.6087 A
          StdDev = 0.7066 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 108.678 deg ; T1  -- T1   2.8991 A

T1  -- O2  -- T1  = 116.921 deg ; T1  -- T1   2.8991 A
T1  -- O2  -- T1  =  24.515 deg ; T1  -- T1   0.7555 A
T1  -- O2  -- T1  = 117.813 deg ; T1  -- T1   3.1065 A
T1  -- O2  -- T1  = 127.467 deg ; T1  -- T1   2.8425 A
T1  -- O2  -- T1  =  24.515 deg ; T1  -- T1   0.7555 A
T1  -- O2  -- T1  = 116.921 deg ; T1  -- T1   2.8991 A

T1  -- O3  -- T1  =  20.679 deg ; T1  -- T1   0.7555 A
T1  -- O3  -- T1  = 149.772 deg ; T1  -- T1   3.4803 A
T1  -- O3  -- T1  = 162.718 deg ; T1  -- T1   3.1701 A
T1  -- O3  -- T1  = 152.452 deg ; T1  -- T1   3.8852 A
T1  -- O3  -- T1  = 149.772 deg ; T1  -- T1   3.4803 A
T1  -- O3  -- T1  =  20.679 deg ; T1  -- T1   0.7555 A


        T-O-T SUMMARY
          Range  = 20.6794° <--> 162.7184 deg
          Mean   = 99.4541 deg
          StdDev = 53.9370 deg

        T--T SUMMARY
          Range  = 0.7555 A <--> 3.8852 A
          Mean   = 2.4372 A
          StdDev = 1.1636 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.2396 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 8 neighboring T-atoms within 3.50 A, but only 6 bridging O-atoms
  T1  -- T1  = 2.8991 Angstrom
  T1  -- T1  = 2.8991 Angstrom
  T1  -- T1  = 0.7555 Angstrom
  T1  -- T1  = 2.8425 Angstrom
  T1  -- T1  = 3.1065 Angstrom
  T1  -- T1  = 3.4803 Angstrom
  T1  -- T1  = 3.1701 Angstrom
  T1  -- T1  = 3.4803 Angstrom