Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_154_2_24042_2UrIWD.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 23.09 T-atoms per nm^3
Material density = 2.304 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6600 Angstrom
T1  -- O4  = 1.6106 Angstrom
T1  -- O3  = 1.5589 Angstrom
T1  -- O2  = 1.6443 Angstrom
      mean = 1.6185 Angstrom
        t1 = 0.077446  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.058473  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6667 Angstrom
T2  -- O3  = 1.5482 Angstrom
T2  -- O4  = 1.6111 Angstrom
T2  -- O5  = 1.6846 Angstrom
      mean = 1.6276 Angstrom
        t1 = 0.065886  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.041372  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5482 A <--> 1.6846 A
          Mean   = 1.6230 A
          StdDev = 0.0473 A

       t1 Range  = 0.0659 <-- 0.0717 --> 0.0774
       t2 Range  = 0.0414 <-- 0.0499 --> 0.0585

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 105.819 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 101.633 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 127.922 deg; O1  -- O2  = 3 A
O4  -- T1  -- O3  = 115.394 deg; O4  -- O3  = 3 A
O4  -- T1  -- O2  = 112.964 deg; O4  -- O2  = 3 A
O3  -- T1  -- O2  =  91.967 deg; O3  -- O2  = 2 A
       91.967 deg <-- 109.283 deg --> 127.922 deg

O2  -- T2  -- O3  = 104.112 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.522 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 123.282 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 103.027 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 100.096 deg; O3  -- O5  = 2 A
O4  -- T2  -- O5  = 114.713 deg; O4  -- O5  = 3 A
       100.096 deg <-- 108.959 deg --> 123.282 deg

        O-T-O SUMMARY
          Range  = 91.9672 deg <--> 127.9221 deg
          Mean   = 109.1210 deg
          StdDev = 9.8352 deg

        O--O SUMMARY
          Range  = 2.3044 A <--> 2.9689 A
          Mean   = 2.6371 A
          StdDev = 0.1902 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O4  - T1  = 107.631 deg; T2  -- T1  = 4.8543 A
T2  - O1  - T1  - O3  - T2  = 108.570 deg; T2  -- T2  = 5.0477 A
T2  - O1  - T1  - O2  - T2  =  91.487 deg; T2  -- T2  = 4.5713 A
T1  - O4  - T1  - O3  - T2  =  82.916 deg; T1  -- T2  = 3.8661 A
T1  - O4  - T1  - O2  - T2  = 158.859 deg; T1  -- T2  = 5.9001 A
T2  - O3  - T1  - O2  - T2  =  99.808 deg; T2  -- T2  = 4.7512 A

T1  - O2  - T2  - O3  - T1  = 100.608 deg; T1  -- T1  = 4.9110 A
T1  - O2  - T2  - O4  - T1  = 113.273 deg; T1  -- T1  = 5.1922 A
T1  - O2  - T2  - O5  - T2  = 110.194 deg; T1  -- T2  = 5.2052 A
T1  - O3  - T2  - O4  - T1  = 100.394 deg; T1  -- T1  = 4.7716 A
T1  - O3  - T2  - O5  - T2  = 147.361 deg; T1  -- T2  = 6.0850 A
T1  - O4  - T2  - O5  - T2  =  77.513 deg; T1  -- T2  = 3.8661 A

        T-T-T SUMMARY
          Range  = 77.5130 deg <--> 158.8593 deg
          Mean   = 108.2178 deg
          StdDev = 22.8518 deg

        T--T SUMMARY
          Range  = 3.8661 A <--> 6.0850 A
          Mean   = 4.9185 A
          StdDev = 0.6427 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 115.870 deg ; T1  -- T1   2.8135 A

T1  -- O2  -- T2  = 148.674 deg ; T1  -- T2   3.1881 A

T1  -- O3  -- T2  = 153.007 deg ; T1  -- T2   3.0213 A

T1  -- O4  -- T2  = 165.071 deg ; T1  -- T2   3.1944 A

T2  -- O5  -- T2  = 138.663 deg ; T2  -- T2   3.1524 A


        T-O-T SUMMARY
          Range  = 115.8702° <--> 165.0712 deg
          Mean   = 144.2571 deg
          StdDev = 16.8138 deg

        T--T SUMMARY
          Range  = 2.8135 A <--> 3.1944 A
          Mean   = 3.0739 A
          StdDev = 0.1469 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

<TD10> = 1269.000
Average ring size = 5.6140