Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_153_2_102148_7pxvyg.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.4349 Angstrom
T1  -- O3  = 1.7411 Angstrom
T1  -- O4  = 1.7156 Angstrom
T1  -- O1  = 1.5845 Angstrom
      mean = 1.6190 Angstrom
        t1 = 0.109827  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.078243  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.4402 Angstrom
T2  -- O3  = 1.7065 Angstrom
T2  -- O5  = 1.6885 Angstrom
T2  -- O3  = 1.8074 Angstrom
T2  -- O4  = 1.7165 Angstrom
      mean = 1.6718 Angstrom

        T-O SUMMARY
          Range  = 1.4349 A <--> 1.8074 A
          Mean   = 1.6483 A
          StdDev = 0.1264 A

       t1 Range  = 0.1098 <-- 0.0549 --> 0.1098
       t2 Range  = 0.0782 <-- 0.0391 --> 0.0782

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  =  95.662 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 103.209 deg; O2  -- O4  = 2 A
O2  -- T1  -- O1  = 102.562 deg; O2  -- O1  = 2 A
O3  -- T1  -- O4  = 133.549 deg; O3  -- O4  = 3 A
O3  -- T1  -- O1  = 114.559 deg; O3  -- O1  = 3 A
O4  -- T1  -- O1  = 102.250 deg; O4  -- O1  = 3 A
       95.662 deg <-- 108.632 deg --> 133.549 deg

O2  -- T2  -- O3  =  96.303 deg; O2  -- O3  = 2 A
O2  -- T2  -- O5  =  93.826 deg; O2  -- O5  = 2 A
O2  -- T2  -- O3  = 133.353 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 101.090 deg; O2  -- O4  = 2 A
O3  -- T2  -- O5  = 119.657 deg; O3  -- O5  = 3 A
O3  -- T2  -- O3  =  40.567 deg; O3  -- O3  = 1 A
O3  -- T2  -- O4  = 117.384 deg; O3  -- O4  = 3 A
O5  -- T2  -- O3  = 120.223 deg; O5  -- O3  = 3 A
O5  -- T2  -- O4  = 118.502 deg; O5  -- O4  = 3 A
O3  -- T2  -- O4  =  90.078 deg; O3  -- O4  = 2 A
       40.567 deg <-- 103.098 deg --> 133.353 deg

        O-T-O SUMMARY
          Range  = 40.5674 deg <--> 133.5487 deg
          Mean   = 105.1732 deg
          StdDev = 21.3038 deg

        O--O SUMMARY
          Range  = 1.2218 A <--> 3.1766 A
          Mean   = 2.5842 A
          StdDev = 0.4531 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 148.325 deg ; T1  -- T1   3.0487 A

T1  -- O2  -- T2  = 125.562 deg ; T1  -- T2   2.5567 A

T1  -- O3  -- T2  = 134.766 deg ; T1  -- T2   3.1825 A
T1  -- O3  -- T2  =  85.027 deg ; T1  -- T2   2.3984 A
T2  -- O3  -- T2  =  96.660 deg ; T2  -- T2   2.6256 A

T1  -- O4  -- T2  = 125.892 deg ; T1  -- T2   3.0566 A

T2  -- O5  -- T2  = 138.840 deg ; T2  -- T2   3.1615 A


        T-O-T SUMMARY
          Range  = 85.0265° <--> 148.3255 deg
          Mean   = 122.1532 deg
          StdDev = 21.5602 deg

        T--T SUMMARY
          Range  = 2.3984 A <--> 3.1825 A
          Mean   = 2.8614 A
          StdDev = 0.3034 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O5  = 2.2912 A
O3  -- O3  = 1.2218 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.7364 Angstrom
  T1  -- T2  = 2.5567 Angstrom
  T1  -- T2  = 2.3984 Angstrom
  T1  -- T2  = 3.1825 Angstrom
  T1  -- T1  = 3.0487 Angstrom
  T1  -- T2  = 3.0566 Angstrom
T2  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T2  -- T1  = 2.5567 Angstrom
  T2  -- T1  = 3.1825 Angstrom
  T2  -- T2  = 3.1615 Angstrom
  T2  -- T1  = 2.3984 Angstrom
  T2  -- T1  = 3.0566 Angstrom
  T2  -- T2  = 2.6256 Angstrom