Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_152_2_84927_XlxpKH.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 24.15 T-atoms per nm^3
Material density = 2.409 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6294 Angstrom
T1  -- O2  = 1.6059 Angstrom
T1  -- O3  = 1.6319 Angstrom
T1  -- O4  = 1.6135 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.013315  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013088  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6041 Angstrom
T2  -- O4  = 1.6155 Angstrom
T2  -- O5  = 1.6299 Angstrom
T2  -- O3  = 1.6306 Angstrom
      mean = 1.6200 Angstrom
        t1 = 0.013350  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010214  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6041 A <--> 1.6319 A
          Mean   = 1.6201 A
          StdDev = 0.0110 A

       t1 Range  = 0.0133 <-- 0.0133 --> 0.0133
       t2 Range  = 0.0102 <-- 0.0117 --> 0.0131

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.254 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.172 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.577 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.756 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.784 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.188 deg; O3  -- O4  = 3 A
       107.784 deg <-- 109.455 deg --> 111.188 deg

O2  -- T2  -- O4  = 108.055 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 107.972 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.467 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 108.679 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 111.264 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 111.292 deg; O5  -- O3  = 3 A
       107.972 deg <-- 109.455 deg --> 111.292 deg

        O-T-O SUMMARY
          Range  = 107.7840 deg <--> 111.2922 deg
          Mean   = 109.4550 deg
          StdDev = 1.3777 deg

        O--O SUMMARY
          Range  = 2.6010 A <--> 2.6918 A
          Mean   = 2.6453 A
          StdDev = 0.0313 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  99.244 deg; T1  -- T2  = 4.3890 A
T1  - O1  - T1  - O3  - T2  =  97.203 deg; T1  -- T2  = 4.5010 A
T1  - O1  - T1  - O4  - T2  = 146.002 deg; T1  -- T2  = 5.7451 A
T2  - O2  - T1  - O3  - T2  = 121.832 deg; T2  -- T2  = 5.2151 A
T2  - O2  - T1  - O4  - T2  = 103.794 deg; T2  -- T2  = 4.7047 A
T2  - O3  - T1  - O4  - T2  =  91.558 deg; T2  -- T2  = 4.4518 A

T1  - O2  - T2  - O4  - T2  =  93.952 deg; T1  -- T2  = 4.2389 A
T1  - O2  - T2  - O5  - T1  = 103.794 deg; T1  -- T1  = 4.7047 A
T1  - O2  - T2  - O3  - T1  = 123.312 deg; T1  -- T1  = 5.2520 A
T2  - O4  - T2  - O5  - T1  = 147.899 deg; T2  -- T1  = 5.8084 A
T2  - O4  - T2  - O3  - T1  =  99.659 deg; T2  -- T1  = 4.6122 A
T1  - O5  - T2  - O3  - T1  =  92.708 deg; T1  -- T1  = 4.4951 A

        T-T-T SUMMARY
          Range  = 91.5583 deg <--> 147.8988 deg
          Mean   = 110.0798 deg
          StdDev = 19.3041 deg

        T--T SUMMARY
          Range  = 4.2389 A <--> 5.8084 A
          Mean   = 4.8432 A
          StdDev = 0.5123 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 125.445 deg ; T1  -- T1   2.8964 A

T1  -- O2  -- T2  = 126.374 deg ; T1  -- T2   2.8649 A

T1  -- O3  -- T2  = 144.914 deg ; T1  -- T2   3.1108 A

T1  -- O4  -- T2  = 147.656 deg ; T1  -- T2   3.1012 A

T2  -- O5  -- T2  = 128.247 deg ; T2  -- T2   2.9330 A


        T-O-T SUMMARY
          Range  = 125.4451° <--> 147.6562 deg
          Mean   = 134.5272 deg
          StdDev = 9.8470 deg

        T--T SUMMARY
          Range  = 2.8649 A <--> 3.1108 A
          Mean   = 2.9813 A
          StdDev = 0.1059 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 24 40 64 96 134 176 221 272 330 392 458 530 614 702
TD10 = 1044
Circuit symbol = 6.6_{2}.6_{2}.6_{4}.6_{3}.6_{3}
Weight = 26
Vertex symbol  = 6.6_{2}.6_{2}.6_{4}.6_{3}.6_{3}
Weight = 26

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 24 40 64 96 134 176 221 272 330 392 458 530 614 702
TD10 = 1044
Circuit symbol = 6.6_{2}.6_{2}.6_{4}.6_{3}.6_{3}
Weight = 26
Vertex symbol  = 6.6_{2}.6_{2}.6_{4}.6_{3}.6_{3}
Weight = 26

<TD10> = 1044.000
Average ring size = 6.0000