Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_152_2_70837_dScorD.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 29.64 T-atoms per nm^3
Material density = 2.957 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6511 Angstrom
T1  -- O2  = 1.6450 Angstrom
T1  -- O3  = 1.5862 Angstrom
T1  -- O4  = 1.5944 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.047662  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.034280  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6404 Angstrom
T2  -- O3  = 1.6729 Angstrom
T2  -- O5  = 1.6363 Angstrom
T2  -- O4  = 1.5879 Angstrom
      mean = 1.6344 Angstrom
        t1 = 0.047168  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033849  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5862 A <--> 1.6729 A
          Mean   = 1.6268 A
          StdDev = 0.0310 A

       t1 Range  = 0.0472 <-- 0.0474 --> 0.0477
       t2 Range  = 0.0338 <-- 0.0341 --> 0.0343

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.493 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 113.498 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.200 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 103.509 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 115.258 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  98.680 deg; O3  -- O4  = 2 A
       98.680 deg <-- 109.273 deg --> 115.258 deg

O2  -- T2  -- O3  = 112.877 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 113.596 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 100.540 deg; O2  -- O4  = 2 A
O3  -- T2  -- O5  = 113.510 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 112.814 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 102.287 deg; O5  -- O4  = 3 A
       100.540 deg <-- 109.271 deg --> 113.596 deg

        O-T-O SUMMARY
          Range  = 98.6803 deg <--> 115.2578 deg
          Mean   = 109.2718 deg
          StdDev = 5.9180 deg

        O--O SUMMARY
          Range  = 2.4128 A <--> 2.7720 A
          Mean   = 2.6508 A
          StdDev = 0.1236 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  91.072 deg; T2  -- T2  = 4.1697 A
T2  - O1  - T1  - O3  - T2  = 147.554 deg; T2  -- T2  = 5.6924 A
T2  - O1  - T1  - O4  - T1  = 110.926 deg; T2  -- T1  = 5.0509 A
T2  - O2  - T1  - O3  - T2  = 118.792 deg; T2  -- T2  = 5.1542 A
T2  - O2  - T1  - O4  - T1  =  84.869 deg; T2  -- T1  = 4.1797 A
T2  - O3  - T1  - O4  - T1  =  85.789 deg; T2  -- T1  = 4.2722 A

T1  - O2  - T2  - O3  - T1  = 138.555 deg; T1  -- T1  = 5.4642 A
T1  - O2  - T2  - O5  - T1  =  85.138 deg; T1  -- T1  = 4.0118 A
T1  - O2  - T2  - O4  - T2  = 111.724 deg; T1  -- T2  = 5.0538 A
T1  - O3  - T2  - O5  - T1  = 134.673 deg; T1  -- T1  = 5.5258 A
T1  - O3  - T2  - O4  - T2  =  87.681 deg; T1  -- T2  = 4.2722 A
T1  - O5  - T2  - O4  - T2  =  83.924 deg; T1  -- T2  = 4.1797 A

        T-T-T SUMMARY
          Range  = 83.9244 deg <--> 147.5542 deg
          Mean   = 106.7248 deg
          StdDev = 22.8142 deg

        T--T SUMMARY
          Range  = 4.0118 A <--> 5.6924 A
          Mean   = 4.7522 A
          StdDev = 0.6053 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.976 deg ; T1  -- T1   3.2358 A

T1  -- O2  -- T2  = 123.286 deg ; T1  -- T2   2.8912 A

T1  -- O3  -- T2  = 129.744 deg ; T1  -- T2   2.9509 A

T1  -- O4  -- T2  = 145.257 deg ; T1  -- T2   3.0372 A

T2  -- O5  -- T2  = 157.725 deg ; T2  -- T2   3.2110 A


        T-O-T SUMMARY
          Range  = 123.2864° <--> 157.7247 deg
          Mean   = 142.5978 deg
          StdDev = 14.2450 deg

        T--T SUMMARY
          Range  = 2.8912 A <--> 3.2358 A
          Mean   = 3.0652 A
          StdDev = 0.1398 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 24 46 78 111 149 193 245 302 368 436 513 593 680 776
TD10 = 1163
Circuit symbol = 4.7_{2}.4.7_{3}.6.7
Weight = 19
Vertex symbol  = 4.7_{2}.4.7_{3}.7.10_{15}
Weight = 38

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 24 46 78 111 149 193 245 302 368 436 513 593 680 776
TD10 = 1163
Circuit symbol = 4.7_{2}.4.7_{3}.6.7
Weight = 19
Vertex symbol  = 4.7_{2}.4.7_{3}.7.10_{15}
Weight = 38

<TD10> = 1163.000
Average ring size = 8.0500