Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_152_2_134176_V72SBR.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 27.01 T-atoms per nm^3
Material density = 2.695 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6210 Angstrom
T1  -- O2  = 1.6203 Angstrom
T1  -- O1  = 1.6210 Angstrom
T1  -- O2  = 1.6203 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.006732  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001468  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6205 Angstrom
T2  -- O1  = 1.6205 Angstrom
T2  -- O2  = 1.6207 Angstrom
T2  -- O2  = 1.6207 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.006724  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001336  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6203 A <--> 1.6210 A
          Mean   = 1.6206 A
          StdDev = 0.0003 A

       t1 Range  = 0.0067 <-- 0.0067 --> 0.0067
       t2 Range  = 0.0013 <-- 0.0014 --> 0.0015

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.322 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 109.129 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.734 deg; O1  -- O2  = 3 A
O2  -- T1  -- O1  = 109.734 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 109.585 deg; O2  -- O2  = 3 A
O1  -- T1  -- O2  = 109.322 deg; O1  -- O2  = 3 A
       109.129 deg <-- 109.471 deg --> 109.734 deg

O1  -- T2  -- O1  = 109.555 deg; O1  -- O1  = 3 A
O1  -- T2  -- O2  = 109.735 deg; O1  -- O2  = 3 A
O1  -- T2  -- O2  = 109.321 deg; O1  -- O2  = 3 A
O1  -- T2  -- O2  = 109.321 deg; O1  -- O2  = 3 A
O1  -- T2  -- O2  = 109.735 deg; O1  -- O2  = 3 A
O2  -- T2  -- O2  = 109.160 deg; O2  -- O2  = 3 A
       109.160 deg <-- 109.471 deg --> 109.735 deg

        O-T-O SUMMARY
          Range  = 109.1290 deg <--> 109.7355 deg
          Mean   = 109.4712 deg
          StdDev = 0.2256 deg

        O--O SUMMARY
          Range  = 2.6414 A <--> 2.6508 A
          Mean   = 2.6464 A
          StdDev = 0.0036 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 143.112 deg; T2  -- T2  = 5.7756 A
T2  - O1  - T1  - O1  - T2  =  90.340 deg; T2  -- T2  = 4.3176 A
T2  - O1  - T1  - O2  - T2  = 107.759 deg; T2  -- T2  = 4.9177 A
T2  - O2  - T1  - O1  - T2  = 107.759 deg; T2  -- T2  = 4.9177 A
T2  - O2  - T1  - O2  - T2  =  90.340 deg; T2  -- T2  = 4.3176 A
T2  - O1  - T1  - O2  - T2  = 121.133 deg; T2  -- T2  = 5.3018 A

T1  - O1  - T2  - O1  - T1  = 143.117 deg; T1  -- T1  = 5.7749 A
T1  - O1  - T2  - O2  - T1  = 107.759 deg; T1  -- T1  = 4.9177 A
T1  - O1  - T2  - O2  - T1  =  90.338 deg; T1  -- T1  = 4.3175 A
T1  - O1  - T2  - O2  - T1  =  90.338 deg; T1  -- T1  = 4.3175 A
T1  - O1  - T2  - O2  - T1  = 107.759 deg; T1  -- T1  = 4.9177 A
T1  - O2  - T2  - O2  - T1  = 121.131 deg; T1  -- T1  = 5.3024 A

        T-T-T SUMMARY
          Range  = 90.3382 deg <--> 143.1167 deg
          Mean   = 110.0737 deg
          StdDev = 18.4021 deg

        T--T SUMMARY
          Range  = 4.3175 A <--> 5.7756 A
          Mean   = 4.9246 A
          StdDev = 0.5206 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 139.806 deg ; T1  -- T2   3.0442 A

T1  -- O2  -- T2  = 139.823 deg ; T1  -- T2   3.0438 A


        T-O-T SUMMARY
          Range  = 139.8064° <--> 139.8232 deg
          Mean   = 139.8148 deg
          StdDev = 0.0092 deg

        T--T SUMMARY
          Range  = 3.0438 A <--> 3.0442 A
          Mean   = 3.0440 A
          StdDev = 0.0002 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 3
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

T2 (Si): multiplicity = 3
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

<TD10> = 1231.000
Average ring size = 7.2727