Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151a_1_93_zfdl2h.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9997 Angstrom
T1  -- O1  = 1.7585 Angstrom
T1  -- O1  = 1.7814 Angstrom
T1  -- O3  = 1.6552 Angstrom
T1  -- O2  = 1.7073 Angstrom
      mean = 1.7804 Angstrom

        T-O SUMMARY
          Range  = 1.6552 A <--> 1.9997 A
          Mean   = 1.7804 A
          StdDev = 0.1200 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  89.233 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  =  77.648 deg; O1  -- O1  = 2 A
O1  -- T1  -- O3  = 138.506 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.394 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 139.304 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  =  86.882 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 121.923 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  78.785 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  =  98.744 deg; O1  -- O2  = 3 A
O3  -- T1  -- O2  = 107.584 deg; O3  -- O2  = 3 A
       77.648 deg <-- 104.800 deg --> 139.304 deg

        O-T-O SUMMARY
          Range  = 77.6480 deg <--> 139.3042 deg
          Mean   = 104.6536 deg
          StdDev = 22.3416 deg

        O--O SUMMARY
          Range  = 2.1831 A <--> 3.4200 A
          Mean   = 2.7744 A
          StdDev = 0.4099 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  74.004 deg ; T1  -- T1   2.2700 A
T1  -- O1  -- T1  =  90.081 deg ; T1  -- T1   2.6800 A
T1  -- O1  -- T1  = 132.493 deg ; T1  -- T1   3.2400 A

T1  -- O2  -- T1  = 141.050 deg ; T1  -- T1   3.2191 A

T1  -- O3  -- T1  = 130.154 deg ; T1  -- T1   3.0021 A


        T-O-T SUMMARY
          Range  = 74.0043° <--> 141.0501 deg
          Mean   = 113.5564 deg
          StdDev = 26.9306 deg

        T--T SUMMARY
          Range  = 2.2700 A <--> 3.2400 A
          Mean   = 2.8822 A
          StdDev = 0.3728 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.1831 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.2400 Angstrom
  T1  -- T1  = 2.2700 Angstrom
  T1  -- T1  = 3.0021 Angstrom
  T1  -- T1  = 2.6800 Angstrom
  T1  -- T1  = 3.2191 Angstrom
  T1  -- T1  = 3.2400 Angstrom