Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151a_1_49_2I7EN1.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.325 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9117 Angstrom
T1  -- O2  = 1.6849 Angstrom
T1  -- O3  = 1.5697 Angstrom
T1  -- O3  = 1.9741 Angstrom
T1  -- O1  = 1.7066 Angstrom
      mean = 1.7694 Angstrom

        T-O SUMMARY
          Range  = 1.5697 A <--> 1.9741 A
          Mean   = 1.7694 A
          StdDev = 0.1530 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 124.115 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 116.323 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  39.633 deg; O1  -- O3  = 1 A
O1  -- T1  -- O1  = 137.355 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 108.511 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 161.294 deg; O2  -- O3  = 4 A
O2  -- T1  -- O1  =  97.537 deg; O2  -- O1  = 3 A
O3  -- T1  -- O3  =  89.827 deg; O3  -- O3  = 3 A
O3  -- T1  -- O1  =  47.238 deg; O3  -- O1  = 1 A
O3  -- T1  -- O1  =  97.731 deg; O3  -- O1  = 3 A
       39.633 deg <-- 101.956 deg --> 161.294 deg

        O-T-O SUMMARY
          Range  = 39.6335 deg <--> 161.2943 deg
          Mean   = 98.7939 deg
          StdDev = 35.7268 deg

        O--O SUMMARY
          Range  = 1.3186 A <--> 3.6106 A
          Mean   = 2.5724 A
          StdDev = 0.7659 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.613 deg ; T1  -- T1   3.2753 A

T1  -- O2  -- T1  = 144.076 deg ; T1  -- T1   3.2056 A

T1  -- O3  -- T1  = 124.400 deg ; T1  -- T1   2.7771 A
T1  -- O3  -- T1  = 134.798 deg ; T1  -- T1   3.2753 A
T1  -- O3  -- T1  =  85.203 deg ; T1  -- T1   2.4171 A
T1  -- O3  -- T1  =  85.202 deg ; T1  -- T1   2.4171 A
T1  -- O3  -- T1  = 134.800 deg ; T1  -- T1   3.2753 A
T1  -- O3  -- T1  =  96.521 deg ; T1  -- T1   2.9460 A


        T-O-T SUMMARY
          Range  = 85.2018° <--> 144.0763 deg
          Mean   = 116.8267 deg
          StdDev = 22.6591 deg

        T--T SUMMARY
          Range  = 2.4171 A <--> 3.2753 A
          Mean   = 2.9486 A
          StdDev = 0.3538 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 1.3186 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.2056 Angstrom
  T1  -- T1  = 2.7771 Angstrom
  T1  -- T1  = 3.2753 Angstrom
  T1  -- T1  = 2.9460 Angstrom
  T1  -- T1  = 2.4171 Angstrom
  T1  -- T1  = 3.2753 Angstrom