Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151a_1_43_3_1C8u.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8924 Angstrom
T1  -- O2  = 1.5607 Angstrom
T1  -- O3  = 1.6846 Angstrom
T1  -- O1  = 1.6869 Angstrom
T1  -- O2  = 2.0031 Angstrom
      mean = 1.7655 Angstrom

        T-O SUMMARY
          Range  = 1.5607 A <--> 2.0031 A
          Mean   = 1.7655 A
          StdDev = 0.1622 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 116.194 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 126.249 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 134.294 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  38.442 deg; O1  -- O2  = 1 A
O2  -- T1  -- O3  = 107.116 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  =  46.479 deg; O2  -- O1  = 1 A
O2  -- T1  -- O2  =  89.379 deg; O2  -- O2  = 3 A
O3  -- T1  -- O1  =  98.490 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 162.998 deg; O3  -- O2  = 4 A
O1  -- T1  -- O2  =  95.898 deg; O1  -- O2  = 3 A
       38.442 deg <-- 101.554 deg --> 162.998 deg

        O-T-O SUMMARY
          Range  = 38.4415 deg <--> 162.9977 deg
          Mean   = 98.3284 deg
          StdDev = 36.0711 deg

        O--O SUMMARY
          Range  = 1.2867 A <--> 3.6474 A
          Mean   = 2.5525 A
          StdDev = 0.7714 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 132.538 deg ; T1  -- T1   3.2776 A

T1  -- O2  -- T1  = 126.050 deg ; T1  -- T1   2.7818 A
T1  -- O2  -- T1  = 133.386 deg ; T1  -- T1   3.2776 A
T1  -- O2  -- T1  =  86.025 deg ; T1  -- T1   2.4525 A
T1  -- O2  -- T1  =  86.027 deg ; T1  -- T1   2.4525 A
T1  -- O2  -- T1  = 133.388 deg ; T1  -- T1   3.2776 A
T1  -- O2  -- T1  =  94.190 deg ; T1  -- T1   2.9344 A

T1  -- O3  -- T1  = 145.118 deg ; T1  -- T1   3.2143 A


        T-O-T SUMMARY
          Range  = 86.0248° <--> 145.1182 deg
          Mean   = 117.0901 deg
          StdDev = 22.8503 deg

        T--T SUMMARY
          Range  = 2.4525 A <--> 3.2776 A
          Mean   = 2.9585 A
          StdDev = 0.3417 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.2866 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 2.7818 Angstrom
  T1  -- T1  = 3.2143 Angstrom
  T1  -- T1  = 3.2776 Angstrom
  T1  -- T1  = 2.9344 Angstrom
  T1  -- T1  = 3.2776 Angstrom
  T1  -- T1  = 2.4525 Angstrom