Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151a_1_197_cZ76EM.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6691 Angstrom
T1  -- O2  = 1.5407 Angstrom
T1  -- O3  = 1.6885 Angstrom
T1  -- O1  = 1.8789 Angstrom
T1  -- O2  = 2.0359 Angstrom
      mean = 1.7626 Angstrom

        T-O SUMMARY
          Range  = 1.5407 A <--> 2.0359 A
          Mean   = 1.7626 A
          StdDev = 0.1772 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  47.056 deg; O1  -- O2  = 1 A
O1  -- T1  -- O3  =  97.219 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 131.967 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  94.041 deg; O1  -- O2  = 3 A
O2  -- T1  -- O3  = 104.890 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 116.128 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  =  88.518 deg; O2  -- O2  = 3 A
O3  -- T1  -- O1  = 129.595 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 166.288 deg; O3  -- O2  = 4 A
O1  -- T1  -- O2  =  38.112 deg; O1  -- O2  = 1 A
       38.112 deg <-- 101.381 deg --> 166.288 deg

        O-T-O SUMMARY
          Range  = 38.1117 deg <--> 166.2876 deg
          Mean   = 98.1135 deg
          StdDev = 36.4621 deg

        O--O SUMMARY
          Range  = 1.2867 A <--> 3.6980 A
          Mean   = 2.5392 A
          StdDev = 0.7706 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 133.629 deg ; T1  -- T1   3.2624 A

T1  -- O2  -- T1  = 131.113 deg ; T1  -- T1   3.2624 A
T1  -- O2  -- T1  = 128.344 deg ; T1  -- T1   2.7736 A
T1  -- O2  -- T1  =  87.363 deg ; T1  -- T1   2.4960 A
T1  -- O2  -- T1  =  87.362 deg ; T1  -- T1   2.4960 A
T1  -- O2  -- T1  =  90.855 deg ; T1  -- T1   2.9006 A
T1  -- O2  -- T1  = 131.112 deg ; T1  -- T1   3.2624 A

T1  -- O3  -- T1  = 150.213 deg ; T1  -- T1   3.2636 A


        T-O-T SUMMARY
          Range  = 87.3616° <--> 150.2127 deg
          Mean   = 117.4988 deg
          StdDev = 23.5516 deg

        T--T SUMMARY
          Range  = 2.4960 A <--> 3.2636 A
          Mean   = 2.9646 A
          StdDev = 0.3266 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.2867 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.2624 Angstrom
  T1  -- T1  = 2.7736 Angstrom
  T1  -- T1  = 2.4960 Angstrom
  T1  -- T1  = 3.2624 Angstrom
  T1  -- T1  = 2.9006 Angstrom
  T1  -- T1  = 3.2636 Angstrom