Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151a_1_137_Gk0qt8.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 2.0072 Angstrom
T1  -- O1  = 1.7953 Angstrom
T1  -- O1  = 1.7624 Angstrom
T1  -- O2  = 1.6596 Angstrom
T1  -- O3  = 1.6994 Angstrom
      mean = 1.7848 Angstrom

        T-O SUMMARY
          Range  = 1.6596 A <--> 2.0072 A
          Mean   = 1.7848 A
          StdDev = 0.1229 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  77.160 deg; O1  -- O1  = 2 A
O1  -- T1  -- O1  =  89.516 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 138.611 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.807 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 139.533 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  79.595 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  99.043 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  =  86.447 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 121.417 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 108.322 deg; O2  -- O3  = 3 A
       77.160 deg <-- 104.845 deg --> 139.533 deg

        O-T-O SUMMARY
          Range  = 77.1603 deg <--> 139.5329 deg
          Mean   = 104.6621 deg
          StdDev = 22.3223 deg

        O--O SUMMARY
          Range  = 2.2139 A <--> 3.4324 A
          Mean   = 2.7816 A
          StdDev = 0.4081 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  90.710 deg ; T1  -- T1   2.7095 A
T1  -- O1  -- T1  =  73.765 deg ; T1  -- T1   2.2709 A
T1  -- O1  -- T1  = 132.668 deg ; T1  -- T1   3.2585 A

T1  -- O2  -- T1  = 130.676 deg ; T1  -- T1   3.0164 A

T1  -- O3  -- T1  = 139.622 deg ; T1  -- T1   3.1900 A


        T-O-T SUMMARY
          Range  = 73.7653° <--> 139.6218 deg
          Mean   = 113.4881 deg
          StdDev = 26.6898 deg

        T--T SUMMARY
          Range  = 2.2709 A <--> 3.2585 A
          Mean   = 2.8891 A
          StdDev = 0.3689 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2139 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.2585 Angstrom
  T1  -- T1  = 3.2585 Angstrom
  T1  -- T1  = 2.7095 Angstrom
  T1  -- T1  = 3.0164 Angstrom
  T1  -- T1  = 2.2709 Angstrom
  T1  -- T1  = 3.1900 Angstrom