Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151a_1_106_0QLhYR.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.32 T-atoms per nm^3
Material density = 3.325 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8780 Angstrom
T1  -- O1  = 1.6656 Angstrom
T1  -- O3  = 2.0901 Angstrom
T1  -- O2  = 1.6902 Angstrom
T1  -- O3  = 1.5232 Angstrom
      mean = 1.7694 Angstrom

        T-O SUMMARY
          Range  = 1.5232 A <--> 2.0901 A
          Mean   = 1.7694 A
          StdDev = 0.1995 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 129.869 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  =  37.812 deg; O1  -- O3  = 1 A
O1  -- T1  -- O2  = 131.981 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 116.064 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  92.463 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  =  96.840 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  47.912 deg; O1  -- O3  = 1 A
O3  -- T1  -- O2  = 168.951 deg; O3  -- O2  = 4 A
O3  -- T1  -- O3  =  87.866 deg; O3  -- O3  = 3 A
O2  -- T1  -- O3  = 102.795 deg; O2  -- O3  = 3 A
       37.812 deg <-- 101.255 deg --> 168.951 deg

        O-T-O SUMMARY
          Range  = 37.8122 deg <--> 168.9509 deg
          Mean   = 97.9703 deg
          StdDev = 36.7258 deg

        O--O SUMMARY
          Range  = 1.3013 A <--> 3.7630 A
          Mean   = 2.5426 A
          StdDev = 0.7704 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.393 deg ; T1  -- T1   3.2677 A

T1  -- O2  -- T1  = 152.856 deg ; T1  -- T1   3.2860 A

T1  -- O3  -- T1  =  88.514 deg ; T1  -- T1   2.5541 A
T1  -- O3  -- T1  = 128.796 deg ; T1  -- T1   3.2677 A
T1  -- O3  -- T1  =  87.592 deg ; T1  -- T1   2.8931 A
T1  -- O3  -- T1  = 130.829 deg ; T1  -- T1   2.7702 A
T1  -- O3  -- T1  = 128.796 deg ; T1  -- T1   3.2677 A
T1  -- O3  -- T1  =  88.514 deg ; T1  -- T1   2.5541 A


        T-O-T SUMMARY
          Range  = 87.5924° <--> 152.8564 deg
          Mean   = 117.5364 deg
          StdDev = 24.0826 deg

        T--T SUMMARY
          Range  = 2.5541 A <--> 3.2860 A
          Mean   = 2.9826 A
          StdDev = 0.3107 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 1.3013 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.2677 Angstrom
  T1  -- T1  = 2.5541 Angstrom
  T1  -- T1  = 2.8931 Angstrom
  T1  -- T1  = 3.2860 Angstrom
  T1  -- T1  = 3.2677 Angstrom
  T1  -- T1  = 2.7702 Angstrom