Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151a_1_103_p3mlSB.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7567 Angstrom
T1  -- O1  = 1.7837 Angstrom
T1  -- O3  = 1.6555 Angstrom
T1  -- O2  = 1.7079 Angstrom
T1  -- O1  = 2.0055 Angstrom
      mean = 1.7819 Angstrom

        T-O SUMMARY
          Range  = 1.6555 A <--> 2.0055 A
          Mean   = 1.7819 A
          StdDev = 0.1221 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 139.381 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  =  87.232 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 121.993 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  =  89.357 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  =  78.708 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  =  98.606 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  =  77.464 deg; O1  -- O1  = 2 A
O3  -- T1  -- O2  = 107.492 deg; O3  -- O2  = 3 A
O3  -- T1  -- O1  = 138.652 deg; O3  -- O1  = 3 A
O2  -- T1  -- O1  = 109.114 deg; O2  -- O1  = 3 A
       77.464 deg <-- 104.800 deg --> 139.381 deg

        O-T-O SUMMARY
          Range  = 77.4638 deg <--> 139.3813 deg
          Mean   = 104.6582 deg
          StdDev = 22.3759 deg

        O--O SUMMARY
          Range  = 2.1831 A <--> 3.4275 A
          Mean   = 2.7767 A
          StdDev = 0.4104 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  90.351 deg ; T1  -- T1   2.6922 A
T1  -- O1  -- T1  = 132.462 deg ; T1  -- T1   3.2402 A
T1  -- O1  -- T1  =  73.881 deg ; T1  -- T1   2.2698 A

T1  -- O2  -- T1  = 140.967 deg ; T1  -- T1   3.2195 A

T1  -- O3  -- T1  = 129.554 deg ; T1  -- T1   2.9953 A


        T-O-T SUMMARY
          Range  = 73.8809° <--> 140.9667 deg
          Mean   = 113.4430 deg
          StdDev = 26.8221 deg

        T--T SUMMARY
          Range  = 2.2698 A <--> 3.2402 A
          Mean   = 2.8834 A
          StdDev = 0.3712 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.1831 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.2402 Angstrom
  T1  -- T1  = 2.2698 Angstrom
  T1  -- T1  = 2.9953 Angstrom
  T1  -- T1  = 3.2195 Angstrom
  T1  -- T1  = 3.2402 Angstrom
  T1  -- T1  = 2.6922 Angstrom