Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_4311434_dvLVAF.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 25.70 T-atoms per nm^3
Material density = 2.565 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6167 Angstrom
T1  -- O2  = 1.6207 Angstrom
T1  -- O3  = 1.6204 Angstrom
T1  -- O4  = 1.6182 Angstrom
      mean = 1.6190 Angstrom
        t1 = 0.005919  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001250  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6177 Angstrom
T2  -- O4  = 1.6217 Angstrom
T2  -- O5  = 1.6177 Angstrom
T2  -- O6  = 1.6198 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.006252  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003117  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6167 A <--> 1.6217 A
          Mean   = 1.6191 A
          StdDev = 0.0017 A

       t1 Range  = 0.0059 <-- 0.0061 --> 0.0063
       t2 Range  = 0.0013 <-- 0.0022 --> 0.0031

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.163 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.483 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.220 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.013 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.299 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.642 deg; O3  -- O4  = 3 A
       109.013 deg <-- 109.470 deg --> 110.220 deg

O3  -- T2  -- O4  = 109.844 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 110.308 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.312 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.273 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.860 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.218 deg; O5  -- O6  = 3 A
       108.860 deg <-- 109.469 deg --> 110.308 deg

        O-T-O SUMMARY
          Range  = 108.8604 deg <--> 110.3085 deg
          Mean   = 109.4950 deg
          StdDev = 0.4487 deg

        O--O SUMMARY
          Range  = 2.6366 A <--> 2.6553 A
          Mean   = 2.6444 A
          StdDev = 0.0061 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 134.033 deg; T1  -- T2  = 5.5549 A
T1  - O1  - T1  - O3  - T1  = 108.042 deg; T1  -- T1  = 4.9955 A
T1  - O1  - T1  - O4  - T2  =  92.992 deg; T1  -- T2  = 4.3769 A
T2  - O2  - T1  - O3  - T1  =  88.521 deg; T2  -- T1  = 4.3885 A
T2  - O2  - T1  - O4  - T2  = 108.654 deg; T2  -- T2  = 4.9955 A
T1  - O3  - T1  - O4  - T2  = 130.202 deg; T1  -- T2  = 5.7021 A

T1  - O3  - T2  - O4  - T2  = 134.039 deg; T1  -- T2  = 5.5549 A
T1  - O3  - T2  - O5  - T1  = 108.654 deg; T1  -- T1  = 4.9955 A
T1  - O3  - T2  - O6  - T2  =  88.528 deg; T1  -- T2  = 4.3891 A
T2  - O4  - T2  - O5  - T1  =  93.000 deg; T2  -- T1  = 4.3775 A
T2  - O4  - T2  - O6  - T2  = 108.020 deg; T2  -- T2  = 4.9955 A
T1  - O5  - T2  - O6  - T2  = 130.204 deg; T1  -- T2  = 5.7031 A

        T-T-T SUMMARY
          Range  = 88.5205 deg <--> 134.0389 deg
          Mean   = 108.4336 deg
          StdDev = 16.5408 deg

        T--T SUMMARY
          Range  = 4.3769 A <--> 5.7031 A
          Mean   = 4.9455 A
          StdDev = 0.4985 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 166.668 deg ; T1  -- T1   3.2115 A

T1  -- O2  -- T1  = 131.800 deg ; T1  -- T1   2.9589 A

T1  -- O3  -- T2  = 143.416 deg ; T1  -- T2   3.0745 A

T1  -- O4  -- T2  = 143.270 deg ; T1  -- T2   3.0749 A

T2  -- O5  -- T2  = 166.266 deg ; T2  -- T2   3.2123 A

T2  -- O6  -- T2  = 131.964 deg ; T2  -- T2   2.9590 A


        T-O-T SUMMARY
          Range  = 131.7998° <--> 166.6678 deg
          Mean   = 147.2305 deg
          StdDev = 14.5891 deg

        T--T SUMMARY
          Range  = 2.9589 A <--> 3.2123 A
          Mean   = 3.0818 A
          StdDev = 0.1049 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

<TD10> = 1231.000
Average ring size = 7.2727