Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_4201386_gWquD4.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 22.23 T-atoms per nm^3
Material density = 2.218 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6159 Angstrom
T1  -- O2  = 1.5445 Angstrom
T1  -- O3  = 1.6751 Angstrom
T1  -- O4  = 1.6613 Angstrom
      mean = 1.6242 Angstrom
        t1 = 0.073146  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048608  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6613 Angstrom
T2  -- O5  = 1.5454 Angstrom
T2  -- O6  = 1.6168 Angstrom
T2  -- O3  = 1.6752 Angstrom
      mean = 1.6247 Angstrom
        t1 = 0.072816  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049357  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5445 A <--> 1.6752 A
          Mean   = 1.6244 A
          StdDev = 0.0513 A

       t1 Range  = 0.0728 <-- 0.0730 --> 0.0731
       t2 Range  = 0.0486 <-- 0.0490 --> 0.0494

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.034 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.306 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.903 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  99.525 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  =  96.500 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 126.385 deg; O3  -- O4  = 3 A
       96.500 deg <-- 108.942 deg --> 126.385 deg

O4  -- T2  -- O5  =  96.536 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 111.769 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 126.342 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 109.368 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  =  99.508 deg; O5  -- O3  = 2 A
O6  -- T2  -- O3  = 110.272 deg; O6  -- O3  = 3 A
       96.536 deg <-- 108.966 deg --> 126.342 deg

        O-T-O SUMMARY
          Range  = 96.4997 deg <--> 126.3848 deg
          Mean   = 108.9314 deg
          StdDev = 10.1401 deg

        O--O SUMMARY
          Range  = 2.3930 A <--> 2.9778 A
          Mean   = 2.6428 A
          StdDev = 0.2009 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  96.572 deg; T1  -- T2  = 4.7946 A
T1  - O1  - T1  - O3  - T2  = 109.048 deg; T1  -- T2  = 5.1050 A
T1  - O1  - T1  - O4  - T1  = 111.146 deg; T1  -- T1  = 5.2065 A
T2  - O2  - T1  - O3  - T2  = 152.779 deg; T2  -- T2  = 6.0557 A
T2  - O2  - T1  - O4  - T1  =  99.787 deg; T2  -- T1  = 4.7997 A
T2  - O3  - T1  - O4  - T1  =  79.814 deg; T2  -- T1  = 3.9257 A

T1  - O4  - T2  - O5  - T2  =  99.824 deg; T1  -- T2  = 4.8025 A
T1  - O4  - T2  - O6  - T2  =  96.304 deg; T1  -- T2  = 4.7864 A
T1  - O4  - T2  - O3  - T1  = 152.874 deg; T1  -- T1  = 6.0569 A
T2  - O5  - T2  - O6  - T2  = 111.163 deg; T2  -- T2  = 5.2108 A
T2  - O5  - T2  - O3  - T1  =  79.782 deg; T2  -- T1  = 3.9257 A
T2  - O6  - T2  - O3  - T1  = 109.228 deg; T2  -- T1  = 5.1128 A

        T-T-T SUMMARY
          Range  = 79.7825 deg <--> 152.8739 deg
          Mean   = 108.5866 deg
          StdDev = 23.4547 deg

        T--T SUMMARY
          Range  = 3.9257 A <--> 6.0569 A
          Mean   = 4.9800 A
          StdDev = 0.6635 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 175.995 deg ; T1  -- T1   3.2298 A

T1  -- O2  -- T1  = 171.991 deg ; T1  -- T1   3.0815 A

T1  -- O3  -- T2  = 130.088 deg ; T1  -- T2   3.0375 A

T1  -- O4  -- T2  = 147.911 deg ; T1  -- T2   3.1931 A

T2  -- O5  -- T2  = 172.114 deg ; T2  -- T2   3.0835 A

T2  -- O6  -- T2  = 176.728 deg ; T2  -- T2   3.2323 A


        T-O-T SUMMARY
          Range  = 130.0877° <--> 176.7281 deg
          Mean   = 162.4711 deg
          StdDev = 17.7143 deg

        T--T SUMMARY
          Range  = 3.0375 A <--> 3.2323 A
          Mean   = 3.1430 A
          StdDev = 0.0791 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

<TD10> = 1269.000
Average ring size = 5.6140