Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_3899326_yBB8bY.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 22.61 T-atoms per nm^3
Material density = 2.256 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6333 Angstrom
T1  -- O3  = 1.4925 Angstrom
T1  -- O2  = 1.6329 Angstrom
T1  -- O4  = 1.6672 Angstrom
      mean = 1.6065 Angstrom
        t1 = 0.066051  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049220  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.4970 Angstrom
T2  -- O4  = 1.6591 Angstrom
T2  -- O5  = 1.6398 Angstrom
T2  -- O6  = 1.6340 Angstrom
      mean = 1.6075 Angstrom
        t1 = 0.061288  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050478  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4925 A <--> 1.6672 A
          Mean   = 1.6070 A
          StdDev = 0.0666 A

       t1 Range  = 0.0613 <-- 0.0637 --> 0.0661
       t2 Range  = 0.0492 <-- 0.0498 --> 0.0505

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 101.557 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 112.841 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 116.528 deg; O1  -- O4  = 3 A
O3  -- T1  -- O2  =  99.543 deg; O3  -- O2  = 2 A
O3  -- T1  -- O4  = 106.726 deg; O3  -- O4  = 3 A
O2  -- T1  -- O4  = 116.589 deg; O2  -- O4  = 3 A
       99.543 deg <-- 108.964 deg --> 116.589 deg

O3  -- T2  -- O4  = 103.490 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 104.627 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 101.370 deg; O3  -- O6  = 2 A
O4  -- T2  -- O5  = 117.409 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 116.665 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 110.776 deg; O5  -- O6  = 3 A
       101.370 deg <-- 109.056 deg --> 117.409 deg

        O-T-O SUMMARY
          Range  = 99.5427 deg <--> 117.4092 deg
          Mean   = 108.7557 deg
          StdDev = 6.8596 deg

        O--O SUMMARY
          Range  = 2.3879 A <--> 2.8189 A
          Mean   = 2.6074 A
          StdDev = 0.1732 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 105.468 deg; T1  -- T2  = 4.6854 A
T1  - O1  - T1  - O2  - T1  = 121.404 deg; T1  -- T1  = 5.0885 A
T1  - O1  - T1  - O4  - T2  = 140.178 deg; T1  -- T2  = 5.8655 A
T2  - O3  - T1  - O2  - T1  =  97.251 deg; T2  -- T1  = 4.2328 A
T2  - O3  - T1  - O4  - T2  = 102.328 deg; T2  -- T2  = 4.7143 A
T1  - O2  - T1  - O4  - T2  =  81.997 deg; T1  -- T2  = 3.9435 A

T1  - O3  - T2  - O4  - T2  =  95.089 deg; T1  -- T2  = 4.3211 A
T1  - O3  - T2  - O5  - T2  =  89.704 deg; T1  -- T2  = 3.9435 A
T1  - O3  - T2  - O6  - T1  = 102.328 deg; T1  -- T1  = 4.7143 A
T2  - O4  - T2  - O5  - T2  = 114.771 deg; T2  -- T2  = 4.8474 A
T2  - O4  - T2  - O6  - T1  = 149.413 deg; T2  -- T1  = 5.9878 A
T2  - O5  - T2  - O6  - T1  =  90.500 deg; T2  -- T1  = 4.2328 A

        T-T-T SUMMARY
          Range  = 81.9965 deg <--> 149.4127 deg
          Mean   = 107.6800 deg
          StdDev = 20.1580 deg

        T--T SUMMARY
          Range  = 3.9435 A <--> 5.9878 A
          Mean   = 4.7197 A
          StdDev = 0.6605 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 136.986 deg ; T1  -- T1   3.0392 A

T1  -- O2  -- T1  = 117.643 deg ; T1  -- T1   2.7940 A

T1  -- O3  -- T2  = 144.410 deg ; T1  -- T2   2.8465 A

T1  -- O4  -- T2  = 148.208 deg ; T1  -- T2   3.1990 A

T2  -- O5  -- T2  = 133.060 deg ; T2  -- T2   3.0083 A

T2  -- O6  -- T2  = 114.204 deg ; T2  -- T2   2.7440 A


        T-O-T SUMMARY
          Range  = 114.2044° <--> 148.2077 deg
          Mean   = 132.4185 deg
          StdDev = 12.8583 deg

        T--T SUMMARY
          Range  = 2.7440 A <--> 3.1990 A
          Mean   = 2.9385 A
          StdDev = 0.1604 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7940 Angstrom
T2  -- T2  = 2.7440 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 36 57 86 121 162 206 254 309 370 438 510 589 672
TD10 = 958
Circuit symbol = 4.6.4.6.6_{2}.8_{11}
Weight = 27
Vertex symbol  = 4.6.4.6.6.8_{7}
Weight = 26

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 36 57 86 121 162 206 254 309 370 438 510 589 672
TD10 = 958
Circuit symbol = 4.6.4.6.6_{2}.8_{11}
Weight = 27
Vertex symbol  = 4.6.4.6.6.8_{7}
Weight = 26

<TD10> = 958.000
Average ring size = 6.4000