Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_3725078_HD5BMN.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 22.40 T-atoms per nm^3
Material density = 2.235 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5547 Angstrom
T1  -- O2  = 1.6072 Angstrom
T1  -- O4  = 1.6770 Angstrom
T1  -- O3  = 1.6575 Angstrom
      mean = 1.6241 Angstrom
        t1 = 0.065517  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.047627  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6785 Angstrom
T2  -- O4  = 1.6657 Angstrom
T2  -- O5  = 1.5262 Angstrom
T2  -- O6  = 1.6290 Angstrom
      mean = 1.6248 Angstrom
        t1 = 0.085891  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.080570  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5262 A <--> 1.6785 A
          Mean   = 1.6245 A
          StdDev = 0.0545 A

       t1 Range  = 0.0655 <-- 0.0757 --> 0.0859
       t2 Range  = 0.0476 <-- 0.0641 --> 0.0806

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.776 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 103.705 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  =  97.273 deg; O1  -- O3  = 2 A
O2  -- T1  -- O4  = 111.503 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 104.999 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 125.719 deg; O4  -- O3  = 3 A
       97.273 deg <-- 109.329 deg --> 125.719 deg

O3  -- T2  -- O4  = 125.956 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  =  95.819 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 116.778 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  =  95.631 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 110.242 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 105.871 deg; O5  -- O6  = 3 A
       95.631 deg <-- 108.383 deg --> 125.956 deg

        O-T-O SUMMARY
          Range  = 95.6307 deg <--> 125.9557 deg
          Mean   = 108.8135 deg
          StdDev = 10.4410 deg

        O--O SUMMARY
          Range  = 2.3670 A <--> 2.9791 A
          Mean   = 2.6408 A
          StdDev = 0.2097 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 114.321 deg; T1  -- T1  = 5.3122 A
T1  - O1  - T1  - O4  - T2  =  78.800 deg; T1  -- T2  = 3.8916 A
T1  - O1  - T1  - O3  - T2  = 100.153 deg; T1  -- T2  = 4.8381 A
T1  - O2  - T1  - O4  - T2  = 115.486 deg; T1  -- T2  = 5.2727 A
T1  - O2  - T1  - O3  - T2  =  89.652 deg; T1  -- T2  = 4.5201 A
T2  - O4  - T1  - O3  - T2  = 153.138 deg; T2  -- T2  = 6.0497 A

T1  - O3  - T2  - O4  - T2  =  99.730 deg; T1  -- T2  = 4.7582 A
T1  - O3  - T2  - O5  - T1  = 151.617 deg; T1  -- T1  = 6.0300 A
T1  - O3  - T2  - O6  - T2  = 102.501 deg; T1  -- T2  = 5.0345 A
T2  - O4  - T2  - O5  - T1  =  80.164 deg; T2  -- T1  = 3.8916 A
T2  - O4  - T2  - O6  - T2  = 108.969 deg; T2  -- T2  = 5.1131 A
T1  - O5  - T2  - O6  - T2  = 104.323 deg; T1  -- T2  = 4.9595 A

        T-T-T SUMMARY
          Range  = 78.8001 deg <--> 153.1377 deg
          Mean   = 108.1393 deg
          StdDev = 23.8219 deg

        T--T SUMMARY
          Range  = 3.8916 A <--> 6.0497 A
          Mean   = 4.9578 A
          StdDev = 0.6830 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.919 deg ; T1  -- T1   3.1093 A

T1  -- O2  -- T1  = 176.465 deg ; T1  -- T1   3.2130 A

T1  -- O3  -- T2  = 147.030 deg ; T1  -- T2   3.1989 A

T1  -- O4  -- T2  = 129.300 deg ; T1  -- T2   3.0208 A

T2  -- O5  -- T2  = 164.084 deg ; T2  -- T2   3.0231 A

T2  -- O6  -- T2  = 176.479 deg ; T2  -- T2   3.2564 A


        T-O-T SUMMARY
          Range  = 129.2997° <--> 178.9190 deg
          Mean   = 162.0461 deg
          StdDev = 18.5298 deg

        T--T SUMMARY
          Range  = 3.0208 A <--> 3.2564 A
          Mean   = 3.1369 A
          StdDev = 0.0936 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

<TD10> = 1269.000
Average ring size = 5.6140