Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_3597740_a7KpGm.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 27.76 T-atoms per nm^3
Material density = 2.770 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5150 Angstrom
T1  -- O2  = 1.6548 Angstrom
T1  -- O3  = 1.7054 Angstrom
T1  -- O4  = 1.6832 Angstrom
      mean = 1.6396 Angstrom
        t1 = 0.101808  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.098922  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6180 Angstrom
T2  -- O5  = 1.5231 Angstrom
T2  -- O3  = 1.7142 Angstrom
T2  -- O4  = 1.6388 Angstrom
      mean = 1.6235 Angstrom
        t1 = 0.100807  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076683  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5150 A <--> 1.7142 A
          Mean   = 1.6316 A
          StdDev = 0.0724 A

       t1 Range  = 0.1008 <-- 0.1013 --> 0.1018
       t2 Range  = 0.0767 <-- 0.0878 --> 0.0989

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  99.287 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  92.078 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  =  96.465 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 119.398 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 113.505 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 124.033 deg; O3  -- O4  = 3 A
       92.078 deg <-- 107.461 deg --> 124.033 deg

O2  -- T2  -- O5  =  91.908 deg; O2  -- O5  = 2 A
O2  -- T2  -- O3  = 113.870 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 101.374 deg; O2  -- O4  = 3 A
O5  -- T2  -- O3  = 112.288 deg; O5  -- O3  = 3 A
O5  -- T2  -- O4  =  98.040 deg; O5  -- O4  = 2 A
O3  -- T2  -- O4  = 131.533 deg; O3  -- O4  = 3 A
       91.908 deg <-- 108.169 deg --> 131.533 deg

        O-T-O SUMMARY
          Range  = 91.9083 deg <--> 131.5329 deg
          Mean   = 107.8148 deg
          StdDev = 12.6315 deg

        O--O SUMMARY
          Range  = 2.2587 A <--> 3.0577 A
          Mean   = 2.6267 A
          StdDev = 0.2682 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 108.988 deg; T1  -- T2  = 4.7983 A
T1  - O1  - T1  - O3  - T2  =  92.526 deg; T1  -- T2  = 4.1785 A
T1  - O1  - T1  - O4  - T2  =  87.825 deg; T1  -- T2  = 4.0397 A
T2  - O2  - T1  - O3  - T2  =  99.542 deg; T2  -- T2  = 4.6762 A
T2  - O2  - T1  - O4  - T2  = 113.387 deg; T2  -- T2  = 5.1508 A
T2  - O3  - T1  - O4  - T2  = 145.019 deg; T2  -- T2  = 5.7728 A

T1  - O2  - T2  - O5  - T1  =  71.245 deg; T1  -- T1  = 3.5681 A
T1  - O2  - T2  - O3  - T2  =  76.323 deg; T1  -- T2  = 3.8003 A
T1  - O2  - T2  - O4  - T1  = 110.159 deg; T1  -- T1  = 5.0534 A
T1  - O5  - T2  - O3  - T2  = 102.505 deg; T1  -- T2  = 4.7102 A
T1  - O5  - T2  - O4  - T1  = 174.171 deg; T1  -- T1  = 6.0448 A
T2  - O3  - T2  - O4  - T1  =  83.307 deg; T2  -- T1  = 4.0397 A

        T-T-T SUMMARY
          Range  = 71.2450 deg <--> 174.1710 deg
          Mean   = 105.4164 deg
          StdDev = 28.2084 deg

        T--T SUMMARY
          Range  = 3.5681 A <--> 6.0448 A
          Mean   = 4.6527 A
          StdDev = 0.7415 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 132.352 deg ; T1  -- T1   2.7719 A

T1  -- O2  -- T2  = 144.523 deg ; T1  -- T2   3.1172 A

T1  -- O3  -- T2  = 125.915 deg ; T1  -- T2   3.0457 A

T1  -- O4  -- T2  = 129.687 deg ; T1  -- T2   3.0069 A

T2  -- O5  -- T2  = 169.122 deg ; T2  -- T2   3.0324 A


        T-O-T SUMMARY
          Range  = 125.9154° <--> 169.1224 deg
          Mean   = 140.3198 deg
          StdDev = 15.9609 deg

        T--T SUMMARY
          Range  = 2.7719 A <--> 3.1172 A
          Mean   = 2.9948 A
          StdDev = 0.1193 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O5  = 2.2587 A
T1  -- T1  = 2.7719 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 41 64 95 137 177 227 288 352 427 510 594 677 778
TD10 = 1065
Circuit symbol = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.4.6_{2}.8.6_{2}.8
Weight = 20

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 41 64 95 137 177 227 288 352 427 510 594 677 778
TD10 = 1065
Circuit symbol = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.4.6_{2}.8.6_{2}.8
Weight = 20

<TD10> = 1065.000
Average ring size = 5.6471