Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_3467664_KyAE81.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 22.59 T-atoms per nm^3
Material density = 2.254 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6339 Angstrom
T1  -- O2  = 1.6402 Angstrom
T1  -- O3  = 1.4971 Angstrom
T1  -- O4  = 1.6589 Angstrom
      mean = 1.6075 Angstrom
        t1 = 0.061368  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061107  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.4925 Angstrom
T2  -- O5  = 1.6327 Angstrom
T2  -- O6  = 1.6329 Angstrom
T2  -- O4  = 1.6671 Angstrom
      mean = 1.6063 Angstrom
        t1 = 0.065970  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.062026  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4925 A <--> 1.6671 A
          Mean   = 1.6069 A
          StdDev = 0.0665 A

       t1 Range  = 0.0614 <-- 0.0637 --> 0.0660
       t2 Range  = 0.0611 <-- 0.0616 --> 0.0620

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.789 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 101.279 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 116.709 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 104.661 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 117.385 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 103.503 deg; O3  -- O4  = 2 A
       101.279 deg <-- 109.054 deg --> 117.385 deg

O3  -- T2  -- O5  =  99.537 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 101.649 deg; O3  -- O6  = 2 A
O3  -- T2  -- O4  = 106.668 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 112.806 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 116.644 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 116.490 deg; O6  -- O4  = 3 A
       99.537 deg <-- 108.966 deg --> 116.644 deg

        O-T-O SUMMARY
          Range  = 99.5365 deg <--> 117.3846 deg
          Mean   = 108.7564 deg
          StdDev = 6.8623 deg

        O--O SUMMARY
          Range  = 2.3876 A <--> 2.8188 A
          Mean   = 2.6073 A
          StdDev = 0.1732 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 114.902 deg; T1  -- T1  = 4.8522 A
T1  - O1  - T1  - O3  - T2  =  89.797 deg; T1  -- T2  = 3.9477 A
T1  - O1  - T1  - O4  - T2  =  90.377 deg; T1  -- T2  = 4.2293 A
T1  - O2  - T1  - O3  - T2  =  95.265 deg; T1  -- T2  = 4.3297 A
T1  - O2  - T1  - O4  - T2  = 149.301 deg; T1  -- T2  = 5.9893 A
T2  - O3  - T1  - O4  - T2  = 102.287 deg; T2  -- T2  = 4.7154 A

T1  - O3  - T2  - O5  - T2  =  97.161 deg; T1  -- T2  = 4.2293 A
T1  - O3  - T2  - O6  - T2  = 105.333 deg; T1  -- T2  = 4.6814 A
T1  - O3  - T2  - O4  - T1  = 102.287 deg; T1  -- T1  = 4.7154 A
T2  - O5  - T2  - O6  - T2  = 121.357 deg; T2  -- T2  = 5.0838 A
T2  - O5  - T2  - O4  - T1  =  82.116 deg; T2  -- T1  = 3.9477 A
T2  - O6  - T2  - O4  - T1  = 140.325 deg; T2  -- T1  = 5.8683 A

        T-T-T SUMMARY
          Range  = 82.1160 deg <--> 149.3010 deg
          Mean   = 106.5798 deg
          StdDev = 20.3934 deg

        T--T SUMMARY
          Range  = 3.9477 A <--> 5.9893 A
          Mean   = 4.6929 A
          StdDev = 0.6674 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 114.203 deg ; T1  -- T1   2.7437 A

T1  -- O2  -- T1  = 133.153 deg ; T1  -- T1   3.0102 A

T1  -- O3  -- T2  = 144.613 deg ; T1  -- T2   2.8482 A

T1  -- O4  -- T2  = 148.417 deg ; T1  -- T2   3.2005 A

T2  -- O5  -- T2  = 117.489 deg ; T2  -- T2   2.7915 A

T2  -- O6  -- T2  = 136.902 deg ; T2  -- T2   3.0377 A


        T-O-T SUMMARY
          Range  = 114.2028° <--> 148.4173 deg
          Mean   = 132.4629 deg
          StdDev = 12.9615 deg

        T--T SUMMARY
          Range  = 2.7437 A <--> 3.2005 A
          Mean   = 2.9386 A
          StdDev = 0.1611 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7437 Angstrom
T2  -- T2  = 2.7915 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 36 57 86 121 162 206 254 309 370 438 510 589 672
TD10 = 958
Circuit symbol = 4.6.4.6.6_{2}.8_{11}
Weight = 27
Vertex symbol  = 4.6.4.6.6.8_{7}
Weight = 26

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 36 57 86 121 162 206 254 309 370 438 510 589 672
TD10 = 958
Circuit symbol = 4.6.4.6.6_{2}.8_{11}
Weight = 27
Vertex symbol  = 4.6.4.6.6.8_{7}
Weight = 26

<TD10> = 958.000
Average ring size = 6.4000