Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_3350402_w31ZCm.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 22.25 T-atoms per nm^3
Material density = 2.220 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6280 Angstrom
T1  -- O2  = 1.5373 Angstrom
T1  -- O3  = 1.6752 Angstrom
T1  -- O4  = 1.6703 Angstrom
      mean = 1.6277 Angstrom
        t1 = 0.078871  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.063953  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6684 Angstrom
T2  -- O5  = 1.6074 Angstrom
T2  -- O6  = 1.5409 Angstrom
T2  -- O3  = 1.6647 Angstrom
      mean = 1.6204 Angstrom
        t1 = 0.071019  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.059742  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5373 A <--> 1.6752 A
          Mean   = 1.6240 A
          StdDev = 0.0543 A

       t1 Range  = 0.0710 <-- 0.0749 --> 0.0789
       t2 Range  = 0.0597 <-- 0.0618 --> 0.0640

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.350 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 116.270 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.629 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  95.508 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  =  98.990 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 125.139 deg; O3  -- O4  = 3 A
       95.508 deg <-- 108.647 deg --> 125.139 deg

O4  -- T2  -- O5  = 112.492 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 100.609 deg; O4  -- O6  = 2 A
O4  -- T2  -- O3  = 126.888 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 113.908 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 104.729 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  =  97.237 deg; O6  -- O3  = 2 A
       97.237 deg <-- 109.311 deg --> 126.888 deg

        O-T-O SUMMARY
          Range  = 95.5084 deg <--> 126.8882 deg
          Mean   = 108.8745 deg
          StdDev = 10.3946 deg

        O--O SUMMARY
          Range  = 2.3799 A <--> 2.9814 A
          Mean   = 2.6411 A
          StdDev = 0.2063 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 109.028 deg; T1  -- T1  = 5.1481 A
T1  - O1  - T1  - O3  - T2  = 104.899 deg; T1  -- T2  = 4.9726 A
T1  - O1  - T1  - O4  - T2  = 102.031 deg; T1  -- T2  = 5.0321 A
T1  - O2  - T1  - O3  - T2  =  79.411 deg; T1  -- T2  = 3.8871 A
T1  - O2  - T1  - O4  - T2  =  99.760 deg; T1  -- T2  = 4.8098 A
T2  - O3  - T1  - O4  - T2  = 151.754 deg; T2  -- T2  = 6.0486 A

T1  - O4  - T2  - O5  - T2  = 115.729 deg; T1  -- T2  = 5.2770 A
T1  - O4  - T2  - O6  - T1  = 152.578 deg; T1  -- T1  = 6.0593 A
T1  - O4  - T2  - O3  - T2  =  79.264 deg; T1  -- T2  = 3.8871 A
T2  - O5  - T2  - O6  - T1  =  89.672 deg; T2  -- T1  = 4.5370 A
T2  - O5  - T2  - O3  - T2  = 114.805 deg; T2  -- T2  = 5.3009 A
T1  - O6  - T2  - O3  - T2  = 100.113 deg; T1  -- T2  = 4.8293 A

        T-T-T SUMMARY
          Range  = 79.2639 deg <--> 152.5779 deg
          Mean   = 109.0632 deg
          StdDev = 23.4989 deg

        T--T SUMMARY
          Range  = 3.8871 A <--> 6.0593 A
          Mean   = 4.9951 A
          StdDev = 0.6828 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 175.182 deg ; T1  -- T1   3.2531 A

T1  -- O2  -- T1  = 172.475 deg ; T1  -- T1   3.0680 A

T1  -- O3  -- T2  = 149.279 deg ; T1  -- T2   3.2205 A

T1  -- O4  -- T2  = 129.232 deg ; T1  -- T2   3.0163 A

T2  -- O5  -- T2  = 177.946 deg ; T2  -- T2   3.2142 A

T2  -- O6  -- T2  = 173.667 deg ; T2  -- T2   3.0772 A


        T-O-T SUMMARY
          Range  = 129.2323° <--> 177.9463 deg
          Mean   = 162.9637 deg
          StdDev = 18.0659 deg

        T--T SUMMARY
          Range  = 3.0163 A <--> 3.2531 A
          Mean   = 3.1416 A
          StdDev = 0.0918 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

<TD10> = 1269.000
Average ring size = 5.6140