Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_3084722_Qk7rQK.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 23.81 T-atoms per nm^3
Material density = 2.376 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6319 Angstrom
T1  -- O4  = 1.6851 Angstrom
T1  -- O1  = 1.5758 Angstrom
T1  -- O3  = 1.6231 Angstrom
      mean = 1.6290 Angstrom
        t1 = 0.078711  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.072449  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6654 Angstrom
T2  -- O3  = 1.6504 Angstrom
T2  -- O4  = 1.6762 Angstrom
T2  -- O5  = 1.4779 Angstrom
      mean = 1.6175 Angstrom
        t1 = 0.126587  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.121467  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4779 A <--> 1.6851 A
          Mean   = 1.6232 A
          StdDev = 0.0645 A

       t1 Range  = 0.0787 <-- 0.1026 --> 0.1266
       t2 Range  = 0.0724 <-- 0.0970 --> 0.1215

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O4  = 123.633 deg; O2  -- O4  = 3 A
O2  -- T1  -- O1  =  97.811 deg; O2  -- O1  = 2 A
O2  -- T1  -- O3  =  99.174 deg; O2  -- O3  = 2 A
O4  -- T1  -- O1  = 103.082 deg; O4  -- O1  = 3 A
O4  -- T1  -- O3  = 124.245 deg; O4  -- O3  = 3 A
O1  -- T1  -- O3  = 104.521 deg; O1  -- O3  = 3 A
       97.811 deg <-- 108.745 deg --> 124.245 deg

O2  -- T2  -- O3  = 118.391 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 122.281 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  =  92.800 deg; O2  -- O5  = 2 A
O3  -- T2  -- O4  = 119.306 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  =  89.514 deg; O3  -- O5  = 2 A
O4  -- T2  -- O5  =  89.157 deg; O4  -- O5  = 2 A
       89.157 deg <-- 105.241 deg --> 122.281 deg

        O-T-O SUMMARY
          Range  = 89.1567 deg <--> 124.2454 deg
          Mean   = 106.9930 deg
          StdDev = 13.2635 deg

        O--O SUMMARY
          Range  = 2.2060 A <--> 2.9266 A
          Mean   = 2.5982 A
          StdDev = 0.2773 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O2  - T1  - O4  - T1  =  73.027 deg; T2  -- T1  = 3.6747 A
T2  - O2  - T1  - O1  - T2  = 150.770 deg; T2  -- T2  = 6.0241 A
T2  - O2  - T1  - O3  - T2  = 140.307 deg; T2  -- T2  = 5.8307 A
T1  - O4  - T1  - O1  - T2  = 102.749 deg; T1  -- T2  = 4.9249 A
T1  - O4  - T1  - O3  - T2  = 107.332 deg; T1  -- T2  = 5.0567 A
T2  - O1  - T1  - O3  - T2  =  68.901 deg; T2  -- T2  = 3.5796 A

T1  - O2  - T2  - O3  - T1  = 100.800 deg; T1  -- T1  = 4.8756 A
T1  - O2  - T2  - O4  - T2  =  98.946 deg; T1  -- T2  = 4.6383 A
T1  - O2  - T2  - O5  - T1  = 142.687 deg; T1  -- T1  = 5.8985 A
T1  - O3  - T2  - O4  - T2  = 103.476 deg; T1  -- T2  = 4.7695 A
T1  - O3  - T2  - O5  - T1  = 116.410 deg; T1  -- T1  = 5.2689 A
T2  - O4  - T2  - O5  - T1  =  75.955 deg; T2  -- T1  = 3.6747 A

        T-T-T SUMMARY
          Range  = 68.9011 deg <--> 150.7703 deg
          Mean   = 106.7801 deg
          StdDev = 26.1472 deg

        T--T SUMMARY
          Range  = 3.5796 A <--> 6.0241 A
          Mean   = 4.8513 A
          StdDev = 0.8269 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 165.543 deg ; T1  -- T1   3.1266 A

T1  -- O2  -- T2  = 148.972 deg ; T1  -- T2   3.1771 A

T1  -- O3  -- T2  = 148.487 deg ; T1  -- T2   3.1505 A

T1  -- O4  -- T2  = 130.151 deg ; T1  -- T2   3.0483 A

T2  -- O5  -- T2  = 162.443 deg ; T2  -- T2   2.9211 A


        T-O-T SUMMARY
          Range  = 130.1506° <--> 165.5426 deg
          Mean   = 151.1189 deg
          StdDev = 12.7642 deg

        T--T SUMMARY
          Range  = 2.9211 A <--> 3.1771 A
          Mean   = 3.0847 A
          StdDev = 0.0940 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O5  = 2.2800 A
O3  -- O5  = 2.2061 A
O4  -- O5  = 2.2183 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 41 64 95 137 177 227 288 352 427 510 594 677 778
TD10 = 1065
Circuit symbol = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.4.6_{2}.8.6_{2}.8
Weight = 20

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 41 64 95 137 177 227 288 352 427 510 594 677 778
TD10 = 1065
Circuit symbol = 4.4.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.4.6_{2}.8.6_{2}.8
Weight = 20

<TD10> = 1065.000
Average ring size = 5.6471